PHYSICAL STATE AND BIODEGRADATION BEHAVIOR OF STARCH-POLYCAPROLACTONE SYSTEMS

The biodegradation behavior of insoluble crystalline polymers depends on both chemical structure and physical state. The physical state is strongly affected by the molding conditions; moreover the presence of natural hydrophylic substances such as starch can further influence the biodegradation process. This paper examines the biotic and abiotic degradation of thick injection-molded parts, made of pure poly-epsilon-caprolactone (PCL) at different molecular weights, and of PCL in the presence of starch in the case of a commercial grade of Mater-Bi, produced by Novamont. The abiotic degradation was studied at 25 and 50 degrees C, whereas the biotic degradation was followed in conditions of SCAS (semicontinuous activated sludges) at 25 and 50 degrees C, soil burial, and controlled composting. The physical-chemical modifications provoked at the surface and in the bulk of the samples by the different types of degradation were determined by differential scanning calorimetry, viscometric and gravimetric analysis, scanning electron microscopy, and dynamic mechanical analysis. The mechanical modifications induced by the different environments were followed by tensile tests. It was demonstrated that the presence of starch significantly increases the apparent biodegradation rate of PCL, making even thick parts of ZI01U compatible with the composting process.