Case Study on Failure of Ball Bearing of an Aeroengine

被引:10
作者
Bhat, R. R. [1 ]
Nandi, Vaisakhi [1 ]
Manohara, V. [1 ]
Suresh, S. V. [1 ]
机构
[1] Hindustan Aeronaut Ltd, Foundry & Forge Div, Cent Mat & Proc Lab, Bangalore 560017, Karnataka, India
关键词
Aircraft; Bearing failure; Failure analysis; Spalling; Scanning electron microscope;
D O I
10.1007/s11668-011-9509-1
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Heavy damage was reported on the outer race and rolling elements of a ball bearing belonging to jet engine of a military aircraft. Flaking type of damage was noticed only at one particular location on the outer race of the bearing and on almost all the balls of the bearing. The inner race and the cage of the bearing were free from any damage. The chemistry, hardness, and microstructure of the bearing components met the specification requirements. In the actual engine assembly, the bearing was mounted on shaft of bevel gear. Careful examination of the inner diameter (ID) of the inner ring of the bearing revealed nonuniform contact marks. The contact marks were observed in the form of discoloration of the ID surface. The nonuniform contact was attributed to eccentricity caused by improper mounting of the bearing onto the shaft of the bevel gear. This resulted in preferential loading, causing flaking at one particular location on the raceway of the outer ring and damage to the balls of the bearing. Hence, it was concluded that the ball bearing had failed because of assembly error after the last repair of the engine.
引用
收藏
页码:631 / 635
页数:5