Selective leaching of vanadium from chromium residue intensified by electric field

被引：64

作者：

Peng, Hao ^{[1
]}

Liu, Zuohua ^{[1
]}

Tao, Changyuan ^{[1
]}

机构：

[1] Chongqing Univ, Chongqing Key Lab Chem Proc Clean Energy & Resour, Coll Chem & Chem Engn, Chongqing 400044, Peoples R China

来源：

JOURNAL OF ENVIRONMENTAL CHEMICAL ENGINEERING | 2015年 / 3卷 / 02期

关键词：

Vanadium; Electric field; Leaching; Kinetics analysis; Activation energy;

D O I：

10.1016/j.jece.2015.03.031

中图分类号：

X [环境科学、安全科学];

学科分类号：

08 ; 0830 ;

摘要：

Electro-oxidation was an environmentally-friendly technology, which could enhance the leaching process of vanadium. A novel process was developed for the selective leaching of vanadium from residue. The effects of reaction temperature, alkali-to-residue mass ratio, contact time and current intensity on leaching of vanadium were studied. Results showed that under the optimal reaction conditions (reaction temperature of 90 degrees C, initial NaOH-to-residue mass ratio of 0.5:1 g/g, contact time of 120 min, liquid to solid ratio of 4 mL/g and current intensity of 1000 A/m(2)), leaching efficiency of vanadium could reach up to 91.7%. The kinetics study revealed that leaching process of vanadium from chromium residue intensified with electric field was interpreted with shrinking core model under chemical reaction control. The apparent activation energy of vanadium dissolution was 10.08 kJ/mol. Crown Copyright (C) 2015 Published by Elsevier Ltd. All rights reserved.

引用

页码：1252 / 1257

页数：6

共 27 条

[21] Energy-Constrained Quality Optimization for Secure Image Transmission in Wireless Sensor Networks [J].

Wang, Wei ;

Peng, Dongming ;

Wang, Honggang ;

Sharif, Hamid ;

Chen, Hsiao-Hwa .

ADVANCES IN MULTIMEDIA, 2007, 2007

[22] Electrochemical decomposition of vanadium slag in concentrated NaOH solution [J].

Wang, Zhonghang ;

Zheng, Shili ;

Wang, Shaona ;

Qin, Yaling ;

Du, Hao ;

Zhang, Yi .

HYDROMETALLURGY, 2015, 151 :51-55

[23] Oxidative leaching of a Vietnamese chromite ore in highly concentrated potassium hydroxide aqueous solution at 300°C and atmospheric [J].

Xu, HB ;

Zheng, SL ;

Zhang, Y ;

Li, ZH ;

Wang, ZK .

MINERALS ENGINEERING, 2005, 18 (05) :527-535

[24] Leaching of vanadium from chromium residue [J].

Yang, Kang ;

Zhang, Xiaoyun ;

Tian, Xueda ;

Yang, Yonglong ;

Chen, Yanbo .

HYDROMETALLURGY, 2010, 103 (1-4) :7-11

[25] Green manufacturing process of chromium compounds [J].

Zhang, Y ;

Li, ZH ;

Qi, T ;

Zheng, SL ;

Li, HQ ;

Xu, HB .

ENVIRONMENTAL PROGRESS, 2005, 24 (01) :44-50

[26] Green metallurgical processing of chromite [J].

Zheng, S. ;

Zhang, Y. ;

Li, Z. ;

Qi, T. ;

Li, H. ;

Xu, H. .

HYDROMETALLURGY, 2006, 82 (3-4) :157-163

[27]

Zhou X., 2009, P IEEE ICC 2009, V2009, P1, DOI DOI 10.1016/J.HYDR0MET.2009.07.008

← 1 2 3 →