THE PASSIVITY OF IRON AND CARBON-STEEL IN ANHYDROUS PROPYLENE CARBONATE SOLUTIONS

被引:18
作者
SHIFLER, DA [1 ]
MORAN, PJ [1 ]
KRUGER, J [1 ]
机构
[1] USN ACAD,DEPT MECH ENGN,ANNAPOLIS,MD 21402
关键词
D O I
10.1016/0010-938X(91)90102-U
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The passivation behavior of high purity iron and 1018 carbon steel in anhydrous propylene carbonate (PC) containing 0.5 M LiClO4 or 0.5 M LiAsF6 was studied. The air-formed film on Fe was stable and protective over a wide applied potential range in perchlorate solutions. Scratch tests showed that both bare Fe and steel passivate in the anhydrous PC solutions of either electrolyte by chemisorption of PC molecules below the oxidation potential of PC (PC(ox). At higher potentials, bare Fe passivates in PC/LiClO4 via the formation of a Fe(ClO4)2 salt film. The air-formed film on carbon steel was protective up to the PC(ox) potential in either electrolyte. Above PC(ox), deterioration of the air-formed film on steel was associated with sulfide surface inclusions. Pits initiated and grew at these inclusion sites. Scratch tests showed slower repassivation of the bare steel by the Fe(ClO4)2 salt film than on iron. Sulfides impeded this repassivation. Above PC(ox), neither the iron or the steel are in passive in PC/LiAsF6 solutions. The higher solubility of the Fe(AsF6)2 salt prevents precipitation of a protective salt film.
引用
收藏
页码:475 / 496
页数:22
相关论文
共 50 条
[41]   EQUILIBRIA IN PROPYLENE CARBONATE SOLUTIONS [J].
HARVEY, JA .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1967, 114 (08) :C193-&
[42]   STRESS-CORROSION CRACKING OF CARBON-STEEL IN ALKALI ALUMINATE SOLUTIONS [J].
ARTEMEV, VI ;
SEREGIN, VI ;
ZHOLOBOVA, EP ;
BELYAEV, VP .
PROTECTION OF METALS, 1979, 15 (01) :45-48
[43]   PITTING OF CARBON-STEEL IN CHLORIDE-CONTAINING ALKALINE-SOLUTIONS [J].
ARTEMEV, VI ;
BORSHCHEVSKII, AM ;
BATUROVA, LP .
JOURNAL OF APPLIED CHEMISTRY OF THE USSR, 1992, 65 (09) :1761-1763
[44]   THE EFFECTS OF WATER ON THE PASSIVE BEHAVIOR OF 1018 CARBON-STEEL IN ORGANIC SOLUTIONS [J].
SHIFLER, DA ;
MORAN, PJ ;
KRUGER, J .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (04) :934-939
[45]   THE BEHAVIOR OF PASSIVE FILMS ON CARBON-STEEL IN SULFURIC-ACID-SOLUTIONS [J].
GUO, XP ;
IMAIZUMI, H ;
KATOH, K .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1995, 383 (1-2) :99-104
[46]   CORROSION STUDY OF A CARBON-STEEL IN NEUTRAL CHLORIDE SOLUTIONS BY IMPEDANCE TECHNIQUES [J].
BONNEL, A ;
DABOSI, F ;
DESLOUIS, C ;
DUPRAT, M ;
KEDDAM, M ;
TRIBOLLET, B .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1983, 130 (04) :753-761
[47]   EFFECT OF AMMONIA AND CORROSION OF CARBON-STEEL IN SOLUTIONS CONTAINING COPPER IONS [J].
BELYAKOVA, AA ;
STRUNKIN, VA ;
TSEITLIN, KL .
PROTECTION OF METALS, 1979, 15 (04) :357-360
[48]   COMPOSITION OF PROTECTIVE FILMS ON CARBON-STEEL IN SODIUM-NITRITE SOLUTIONS [J].
KOVALENKO, SG ;
KHARITONOV, YY ;
AKOLZIN, AP .
PROTECTION OF METALS, 1985, 21 (04) :488-490
[49]   THE BEHAVIOR OF CARBON-STEEL IN WEAK-ACID AQUEOUS-SOLUTIONS [J].
GRUSHANIN, AI ;
KRUTIKOV, PG ;
KOSTIN, AB ;
LAPINA, GV .
THERMAL ENGINEERING, 1986, 33 (08) :449-451
[50]   THE ANODIC POLARIZATION BEHAVIOR OF CARBON-STEEL IN HOT CAUSTIC ALUMINATE SOLUTIONS [J].
SRIRAM, R ;
TROMANS, D .
CORROSION SCIENCE, 1985, 25 (02) :79-91