FUNCTIONALIZATION OF CARBON-FIBERS

被引:8
|
作者
PALMA, E [1 ]
IBARRA, L [1 ]
机构
[1] CSIC,INST CIENCIA & TECNOL POLIMEROS,JUAN DE LA CIERVA 3,E-28006 MADRID,SPAIN
来源
关键词
D O I
10.1002/apmc.1994.052200110
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
This work reports on a study conducted to achieve carbon fibre functionalization by means of a diazide derivative (p-(azidosulfonyl)benzoyl azide) in two stages. The first stage comprises surface oxidation of the fibres, which causes an increase of the number of superficial COOH groups. During the second stage the oxidated fibres are brought to react with the diazide derivative via the isocyanate group, obtained by means of the Curtius transposition of the carbonyl azide group. Fibre oxidation depends on reaction time, following a similar pattern as the one described for carbon black particles. Oxidized fibre functionalization is evidenced both in the progressive decrease in SO2N3 groups in the reagent solution and through differential scanning calorimetry analysis (DSC), which shows an exothermal peak around 190-degrees-C due to the decomposition of the azide grafted onto the carbon fibre. The degree of attainable functionalization is a function of COOH group concentration, generated during fibre oxidation, and the ratio of the functionalizing agent with regard to the carboxy groups formed.
引用
收藏
页码:111 / 122
页数:12
相关论文
共 50 条
  • [21] FUTURE OF CARBON-FIBERS
    BERKOVITCH, I
    RECHERCHE, 1974, 5 (46): : 574 - 576
  • [22] COATING OF CARBON-FIBERS - THE STRENGTH OF THE FIBERS
    HELMER, T
    PETERLIK, H
    KROMP, K
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (01) : 133 - 136
  • [23] GRAPHITE-FIBERS AND CARBON-FIBERS
    不详
    GUMMI ASBEST KUNSTSTOFFE, 1977, 30 (06): : 369 - &
  • [24] IRON TREATED ACTIVATED CARBON-FIBERS AS NO ADSORBENTS - EFFECT OF THE NATURE OF ACTIVATED CARBON-FIBERS
    KANEKO, K
    OZEKI, S
    INOUYE, K
    NIPPON KAGAKU KAISHI, 1985, (12) : 2315 - 2322
  • [25] CARBON NANOCAPSULES GROWN ON CARBON-FIBERS
    KUSUNOKI, M
    IKUHARA, Y
    KON, J
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1995, 34 (03): : 1610 - 1614
  • [26] UREASE ADSORPTION ON CARBON-FIBERS
    DAVIDENKO, TI
    SEVASTYANOVA, EV
    MOROZOVA, AA
    ANDRONATI, SA
    ERMOLENKO, IN
    YUODVALKITE, DY
    GLEMZHA, AA
    DOPOVIDI AKADEMII NAUK UKRAINSKOI RSR SERIYA B-GEOLOGICHNI KHIMICHNI TA BIOLOGICHNI NAUKI, 1985, (01): : 56 - 59
  • [27] COMPRESSIVE STRENGTH OF CARBON-FIBERS
    PRANDY, JM
    HAHN, HT
    SAMPE QUARTERLY-SOCIETY FOR THE ADVANCEMENT OF MATERIAL AND PROCESS ENGINEERING, 1991, 22 (02): : 47 - 52
  • [28] TENSILE STRENGTHS OF CARBON-FIBERS
    MORETON, R
    WATT, W
    NATURE, 1974, 247 (5440) : 360 - 361
  • [29] BORON MODIFICATION OF CARBON-FIBERS
    AGRAWAL, A
    YINNON, H
    UHLMANN, DR
    PEPPER, RT
    DESPER, CR
    JOURNAL OF MATERIALS SCIENCE, 1986, 21 (10) : 3455 - 3466
  • [30] THE EVALUATION OF CURRENT CARBON-FIBERS
    HUGHES, JDH
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1987, 20 (03) : 276 - 285