Highsilicone Austempered Ductile Iron

被引：2

作者：

Kochanski, A. ^{[1
]}

Krzynska, A. ^{[1
]}

Radziszewski, T. ^{[1
]}

机构：

[1] Warsaw Univ Technol, Inst Technol, Fac Prod Engn, Narbutta 85, PL-02524 Warsaw, Poland

来源：

ARCHIVES OF FOUNDRY ENGINEERING | 2014年 / 14卷 / 01期

关键词：

Austempered ductile iron; Silicone content; Matrix structure; Mechanical properties; Ultimate tensile strength;

D O I：

10.2478/afe-2014-0013

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Ductile iron casts with a higher silicone content were produced. The austempering process of high silicone ductile iron involving different austempering times was studied and the results presented. The results of metallographical observations and tensile strength tests were offered. The obtained results point to the fact that the silicone content which is considered as acceptable in the literature may in fact be exceeded. The issue is viewed as requiring further research.

引用

页码：55 / 58

页数：4

共 19 条

[1] INFLUENCE OF MICROSTRUCTURE ON HIGH-CYCLE FATIGUE BEHAVIOR OF AUSTEMPERED DUCTILE CAST-IRON [J].

BARTOSIEWICZ, L ;

KRAUSE, AR ;

ALBERTS, FA ;

SINGH, I ;

PUTATUNDA, SK .

MATERIALS CHARACTERIZATION, 1993, 30 (04) :221-234

[2]

Bartosiewicz L, 1991, MORR FIN S TMS DETR, P135

[3]

Bartosiewicz L., 1990, P INT S TEST FAIL AN, V16, P323

[4]

Bradenberg K. R., 2002, 2002010674 SAE

[5] FRACTURE-TOUGHNESS OF BAINITIC NODULAR CAST-IRON [J].

DOONG, JL ;

CHEN, CS .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1989, 12 (02) :155-165

[6]

Dorazil E., 1991, P WORLD C AUST DUCT, P32

[7]

Gundlach R.B., 1983, AFS T, V94, P377

[8]

Harding R.A., 1986, BR FOUNDRYMAN, V79, P489

[9]

JOHANSSON M, 1977, AFS T, V85, P117

[10]

Myszka D., 2003, AUSTEMPERED DUCTILE

← 1 2 →