Optimization of cold and warm workability in stainless steel type AISI 316L using instability maps

被引:28
作者
Venugopal, S
Mannan, SL
Prasad, YVRK
机构
[1] INDIRA GANDHI CTR ATOM RES,DIV MAT DEV,KALPAKKAM 603102,TAMIL NADU,INDIA
[2] INDIAN INST SCI,DEPT MET,BANGALORE 560012,KARNATAKA,INDIA
关键词
D O I
10.1016/0022-3115(95)00154-9
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The deformation characteristics of stainless steel type AISI 316L under compression in the temperature range 20 to 600 degrees C and strain rate range 0.001 to 100 s(-1) have been studied with a view to characterizing the flow instabilities occurring in the microstructure. At temperatures lower than 100 degrees C and strain rates higher than 0.1 s(-1), 316L stainless steel exhibits flow localization whereas dynamic strain aging (DSA) occurs at intermediate temperatures and below 1 s(-1). To avoid the above flow instabilities, cold working should be carried out at strain rates less than 0.1 s(-1). Warm working of stainless steel type AISI 316L may be done in the temperature and strain rate regime of: 300 to 400 degrees C and 0.001 s(-1) 300 to 450 degrees C and 0.01 s(-1): 450 to 600 degrees C and 0.1 s(-1); 500 degrees C and 1 s(-1) since these regions are free from flow instabilities like DSA and flow localization. The continuum criterion, developed on the basis of the principles of maximum rate of entropy production and separability of the dissipation function, predicts accurately all the above instability features.
引用
收藏
页码:1 / 10
页数:10
相关论文
共 53 条
[1]  
ALBERTINI C, 1992, PROCESSING METALLURG, P101
[2]  
ALEXANDER JM, 1984, MODELING HOT DEFORMA, P101
[3]   PROCESSING MAP FOR HOT-WORKING OF ALPHA-ZIRCONIUM [J].
CHAKRAVARTTY, JK ;
PRASAD, YVRK ;
ASUNDI, MK .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (04) :829-836
[4]  
CHAKRAVARTTY JK, 1992, ASTM STP, V1132, P48
[5]  
COCKROFT MG, 1968, DUCTILITY, P653
[6]  
de Almeida L H, 1986, STRENGTH METALS ALLO, V1, P337
[7]  
DORAIVELU SM, 1979, THESIS INDIAN I TECH
[8]  
FROST HJ, 1982, DEFORMATION MECHANIS
[9]  
GARAFALO F, 1963, JOINT INT C CREEP, P1
[10]  
GEGEL HL, 1987, METALS HDB, V14, P417