THE EFFECT OF MOLYBDENUM ON THE CORROSION BEHAVIOR OF STEEL ALLOY IN SEA-WATER

被引:1
作者
ALARIFI, A [1 ]
ELDAHSHAN, ME [1 ]
HAZZAA, MI [1 ]
机构
[1] KING SAUD UNIV,DEPT CHEM ENGN,RIYADH 11421,SAUDI ARABIA
关键词
D O I
10.1016/0011-9164(94)00076-X
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The present paper is part of a research program aimed at determining the role played by the molybdenum in steel alloys, Seven different iron-base alloys were used containing molybdenum in the range of 0% to 25% wt. Various corrosion techniques were employed, including: weight loss measurements in static conditions for 3.5% NaCl and Gulf seawater and quiescent flow conditions with Atlantic seawater, electrochemical measurements (LPR and Tafel Plot) under static and dynamic conditions using 3.5% NaCl and Gulf seawater. The tested samples in all cases were investigated by metallography. The preliminary results indicated that an increase in molybdenum level does not affect the corrosion rate, and that molybdenum alone, in the absence of chromium, is not as effective as originally believed, whilst in the presence of chromium it acts as a triggering agent to enhance the action of the chromium.
引用
收藏
页码:77 / 86
页数:10
相关论文
共 50 条
[41]   CORROSION BEHAVIOR OF THERMO-SPRAYED ALUMINUM COATS IN SEA-WATER [J].
FRIEHE, W .
STAHL UND EISEN, 1985, 105 (12) :696-700
[42]   DETERMINATION OF MOLYBDENUM IN SEA-WATER BY EPR SPECTROSCOPY [J].
HANSON, G ;
SZABO, A ;
CHASTEEN, ND .
ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1977, 173 (MAR20) :15-15
[43]   INHIBITORY EFFECT OF ACRYLONITRILE ON COPPER-ZINC ALLOY CORROSION (OT-60) IN SEA-WATER [J].
MOR, ED ;
BECCARIA, AM .
CORROSION TRAITEMENTS PROTECTION FINITION, 1972, 20 (07) :460-&
[44]   COPPER ALLOY PIPES FOR HEAT-EXCHANGERS - THE CORROSION BEHAVIOR OF SAND-BLASTED SURFACES IN SEA-WATER [J].
BARBERY, J ;
PEPINDONAT, C .
METALL, 1982, 36 (11) :1181-1184
[45]   EFFECT OF FLOW ON CORROSION OF COPPER-NICKEL-ALLOYS IN AERATED SEA-WATER AND IN SULFIDE-POLLUTED SEA-WATER [J].
SYRETT, BC ;
WING, SS .
CORROSION, 1980, 36 (02) :73-85
[46]   CORROSION OF STEEL IN SEA-WATER DUE TO ALTERNATING-CURRENT AT 50 HZ [J].
RADEKA, R ;
DABIC, M ;
ZOROVIC, D ;
BARISIN, D .
ANTI-CORROSION METHODS AND MATERIALS, 1977, 24 (09) :5-+
[47]   THE FORMATION OF CALCAREOUS DEPOSITS DURING THE CORROSION OF MILD-STEEL IN SEA-WATER [J].
ELBEIK, S ;
TSEUNG, ACC ;
MACKAY, AL .
CORROSION SCIENCE, 1986, 26 (09) :669-680
[48]   CORROSION OF STAINLESS-STEEL HEAT-EXCHANGE PLANT IN SEA-WATER [J].
LEBEDEV, AN ;
DYAKOV, AA .
THERMAL ENGINEERING, 1975, 22 (06) :73-74
[49]   GROOVING CORROSION IN ELECTRIC-RESISTANCE WELDED STEEL PIPE IN SEA-WATER [J].
KATO, C ;
OTOGURO, Y ;
KADO, S ;
HISAMATSU, Y .
CORROSION SCIENCE, 1978, 18 (01) :61-&
[50]   ACIDIFICATION OF ELECTROLYTE WITHIN CORROSION FATIGUE CRACKS OF 1018 STEEL IN SEA-WATER [J].
HARTT, WH ;
HENKE, TE ;
FLUET, JE .
CORROSION, 1977, 33 (04) :151-152