DIRECT OBSERVATION OF GAMMA -] ALPHA' ISOTHERMAL MARTENSITIC-TRANSFORMATION OF IRON-ALLOYS IN ELECTRON-MICROSCOPE

被引：7

作者：

ARAKI, T ^{[1
]}

SHIBATA, K ^{[1
]}

ASAKURA, K ^{[1
]}

WADA, H ^{[1
]}

机构：

[1] UNIV TOKYO,DEPT MET & MAT SCI,TOKYO,JAPAN

来源：

TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1975年 / 15卷 / 04期

关键词：

IRON NICKEL ALLOYS;

D O I：

10.2355/isijinternational1966.15.175

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Three ternary Fe-25Ni-X alloys with very low C and N contents were investigated, where X equals 2. 7Cr, 4. 5Mo, and 2. 2Mn, respectively. Nucleation of martensite in virgin austenite was not detected. Two levels of growth rate of isothermal martensite were observed; i. e. , 1 to 10 mu m/sec and less than 0. 1 mu m/min. Intermittent motions of dislocations at and in front of the tip of the growing laths were revealed by using the cinephotographic technique. The different types of dislocations observed are discussed.

引用

页码：175 / 184

页数：10

共 22 条

[1]

ARAKI T, 1974, TETSU TO HAGANE, V60, P647

[2]

ARAKI T, 1974, TETSU TO HAGANE, V60, P258

[3]

BEISSWENGER VH, 1956, ARCH EISENHUTTENW, V27, P413

[4] PARTIAL DISLOCATIONS ON (110) PLANES IN BCC LATTICE + TRANSITION OF FCC INTO BCC LATTICE [J].

BOGERS, AJ ;

BURGERS, WG .

ACTA METALLURGICA, 1964, 12 (02) :255-&

[5]

BUNSHAH RF, 1953, T AM I MIN MET ENG, V197, P1251

[6]

Cohen M, 1949, THERMODYNAMICS PHYSI, P242

[7] NUCLEATION AND GROWTH OF MARTENSITE IN FE-32.3 PERCENT NI ALLOY [J].

DASH, S ;

BROWN, N .

ACTA METALLURGICA, 1966, 14 (05) :595-+

[8] CRYSTALLOGRAPHY OF FERROUS MARTENSITES [J].

DUNNE, DP ;

WAYMAN, CM .

METALLURGICAL TRANSACTIONS, 1971, 2 (09) :2327-&

[9]

JASWON MA, 1956, 18 I MET MON, P173

[10] THERMODYNAMICS AND KINETICS OF MARTENSITIC TRANSFORMATIONS [J].

KAUFMAN, L ;

COHEN, M .

PROGRESS IN METAL PHYSICS, 1958, 7 :165-246

← 1 2 3 →