THE STRESS-CORROSION CRACKING OF HIGH-STRENGTH CR-MN-SI-NI AND CR-MO STEELS

被引：4
|
作者：
MAZUR, A
PAWLOWSKI, B
机构：
来源：
CORROSION SCIENCE | 1986年 / 26卷 / 01期
关键词：
D O I：
10.1016/0010-938X(86)90118-6
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
引用
收藏
页码：7 / 14
页数：8
相关论文
共 50 条
  • [1] EFFECT OF MICROSTRUCTURE ON STRESS-CORROSION CRACKING OF CR-MN-SI-NI STEEL
    PAWLOWSKI, B
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1986, 37 (08): : 448 - 451
  • [2] SULFIDE STRESS CRACKING OF HIGH-STRENGTH MODIFIED CR-MO STEELS
    CHARBONNIER, JC
    MARGOTMARETTE, H
    BRASS, AM
    AUCOUTURIER, M
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (05): : 935 - 944
  • [3] METALLURGICAL FACTORS INFLUENCING STRESS-CORROSION CRACKING OF HIGH-STRENGTH NI-CR-MO STEEL WELDS
    METZBOWER, EA
    STOOP, J
    FUJII, CT
    FRASER, FW
    JOURNAL OF METALS, 1978, 30 (10): : 15 - 20
  • [4] STRESS-CORROSION CRACKING CRITERIA FOR HIGH-STRENGTH STEELS
    KARLINSKI, W
    SZACHNOWSKI, W
    BRITISH CORROSION JOURNAL, 1995, 30 (02): : 116 - 118
  • [5] STRESS-CORROSION CRACKING AND CORROSION FATIGUE IN CR-MO LOW-ALLOY STEEL
    AIYAMA, S
    SHOJI, T
    TAKAHASHI, H
    SUZUKI, M
    CORROSION, 1978, 34 (10) : 325 - 331
  • [6] INVESTIGATION OF MECHANISM OF STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEELS
    MARICHEV, YA
    ROSENFELD, IL
    CORROSION, 1976, 32 (11) : 423 - 429
  • [7] EFFECT OF STRENGTH AND MICROSTRUCTURE ON SULFIDE STRESS CRACKING RESISTANCE OF CR-MO STEELS
    FLETCHER, FB
    JOM-JOURNAL OF METALS, 1975, 27 (12): : A40 - A40
  • [8] STRESS-CORROSION CRACKING OF HIGH-STRENGTH STEELS IN AQUEOUS ENVIRONMENTS
    CHU, HC
    GAO, M
    WEI, RP
    JOURNAL OF METALS, 1988, 40 (07): : A67 - A67
  • [9] STRESS-CORROSION CRACKING OF HIGH-STRENGTH STEELS IN AQUEOUS ENVIRONMENTS
    CHU, HC
    WEI, RP
    CORROSION, 1990, 46 (06) : 468 - 476
  • [10] Corrosion of High-Strength Cr–Mn Steels in Chloride Solutions
    A. I. Balitskii
    O. A. Krohmalny
    V. I. Pokhmurskii
    Protection of Metals, 2003, 39 : 34 - 38
12345