DISSOLUTION OF ZRSIO4 AFTER MECHANICAL MILLING WITH AL2O3

被引：17
|
作者：
PUCLIN, T
KACZMAREK, WA
NINHAM, BW
机构：
[1] Institute of Advanced Studies, Research School of Physical Sciences and Engineering, The Australian National University, Canberra
来源：
MATERIALS CHEMISTRY AND PHYSICS | 1995年 / 40卷 / 02期
关键词：
ZIRCON DECOMPOSITION; MECHANOCHEMICAL PROCESSING; MECHANICAL MILLING;
D O I：
10.1016/0254-0584(94)01459-T
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A mixture of alumina (Al2O3) and zircon (ZrSiO4) was subjected to mechanical milling. The presence of alumina was found to greatly enhance the disordering of zircon. Acid leaching of the milled oxide mixtures resulted in complete dissolution of the zirconium, along with a proportion of alumina and only traces of silica. Zirconium leaching was not possible with zircon milled alone. Quantitative results of the leaching process are given.
引用
收藏
页码：105 / 109
页数：5
相关论文
共 50 条
  • [31] ZrSiO4/α-Al2O3反应烧结过程中非晶态物质的形成与演化
    赵世柯
    黄勇
    汪长安
    黄校先
    郭景坤
    无机材料学报, 2003, (01) : 98 - 102
  • [32] Ageing behavior of Al-4.5 wt% Cu matrix alloy reinforced with Al2O3 and ZrSiO4 particulate varying particle size
    Das, Sanjeev
    Das, S.
    Das, K.
    JOURNAL OF MATERIALS SCIENCE, 2006, 41 (16) : 5402 - 5406
  • [33] MULLITE-ZRO2 CERAMICS MADE FROM AL2O3 AND ZRO2/ZRSIO4 PARTICLES COATED WITH AMORPHOUS SILICA
    SHYU, JJ
    CHEN, YC
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1995, 14 (09) : 609 - 612
  • [34] Plasma spray dissociation ZrSiO4 as the basis of forming ZrO2-mullite composites from a ZrSiO4+Al2O3 mixture
    Li, Y
    Khor, KA
    THERMAL SPRAY 2001: NEW SURFACES FOR A NEW MILLENNIUM, 2001, : 237 - 243
  • [35] Transition of γ-Al2O3 into α-Al2O3 during vibro milling
    Kostic, E
    Kiss, SJ
    Zec, S
    Boskovic, S
    POWDER TECHNOLOGY, 2000, 107 (1-2) : 48 - 53
  • [36] Preparation and characterisation of α-Al2O3 powder from γ-Al2O3 powder using mechanical milling technique
    Bodaghi, M.
    Mirhabibi, A. R.
    Zolfonoon, H.
    Salehie, M.
    Tahriri, M.
    MATERIALS RESEARCH INNOVATIONS, 2008, 12 (04) : 157 - 161
  • [37] Enhancing zircon (ZrSiO4) dissolution by ambient temperature processing
    Welham, N.J.
    AusIMM Proceedings, 2001, 306 (02): : 1 - 3
  • [38] Enhancement of Carbothermic Reduction of Al2O3 via Mechanical Milling
    Setiawan, Asep Ridwan
    Ohtsuka, Makoto
    Fukuyama, Hiroyuki
    4TH NANOSCIENCE AND NANOTECHNOLOGY SYMPOSIUM (NNS2011): AN INTERNATIONAL SYMPOSIUM, 2011, 1415
  • [39] Coordinative Crystallization of ZrSiO4 and α-Fe2O3 Composites and Their Resultant Structural, Morphological, and Mechanical Characteristics
    Udaykiran, Roopavath
    Vasanthavel, Subramaniyan
    Kannan, Sanjeevi
    CRYSTAL GROWTH & DESIGN, 2015, 15 (08) : 4075 - 4086
  • [40] Microstructure and Magnetic Properties of Fe/ZrSiO4 Composites Prepared by Mechanical Milling and Spark Plasma Sintering
    Hu, Wentao
    Fan, Xi'an
    Luo, Zigui
    Luo, Fan
    Li, Guangqiang
    Li, Yawei
    Wang, Jian
    IEEE TRANSACTIONS ON MAGNETICS, 2019, 55 (12)
12345