DISSOLUTION OF ZRSIO4 AFTER MECHANICAL MILLING WITH AL2O3

被引：17
|
作者：
PUCLIN, T
KACZMAREK, WA
NINHAM, BW
机构：
[1] Institute of Advanced Studies, Research School of Physical Sciences and Engineering, The Australian National University, Canberra
来源：
MATERIALS CHEMISTRY AND PHYSICS | 1995年 / 40卷 / 02期
关键词：
ZIRCON DECOMPOSITION; MECHANOCHEMICAL PROCESSING; MECHANICAL MILLING;
D O I：
10.1016/0254-0584(94)01459-T
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A mixture of alumina (Al2O3) and zircon (ZrSiO4) was subjected to mechanical milling. The presence of alumina was found to greatly enhance the disordering of zircon. Acid leaching of the milled oxide mixtures resulted in complete dissolution of the zirconium, along with a proportion of alumina and only traces of silica. Zirconium leaching was not possible with zircon milled alone. Quantitative results of the leaching process are given.
引用
收藏
页码：105 / 109
页数：5
相关论文
共 50 条
  • [21] Formation and evolution of noncrystalline phase in reaction-sintering of ZrSiO4/α-Al2O3 mixed powder
    Zhao, SK
    Huang, Y
    Wang, CA
    Huang, XX
    Guo, JK
    JOURNAL OF INORGANIC MATERIALS, 2003, 18 (01) : 98 - 102
  • [22] α-Case formation in Ti-6Al-4V investment casting using ZrSiO4 and AL2O3 moulds
    Chamorro, X.
    Herrero-Dorca, N.
    Rodriguez, P. P.
    Andres, U.
    Azpilgain, Z.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2017, 243 : 75 - 81
  • [23] ZrSiO4/Al2O3复相耐磨陶瓷球的烧结工艺研究
    耿铂
    闫法强
    陈学江
    现代技术陶瓷, 2008, 29 (04) : 3 - 6
  • [24] ZrSiO4/Al2O3/SiO2混合粉体的反应烧结研究
    赵世柯
    赵建东
    肖东梅
    康金生
    真空电子技术, 2005, (04) : 34 - 36+47
  • [25] Mechanical and thermal properties of ZrSiO4
    Nakamori, Fumihiro
    Ohishi, Yuji
    Muta, Hiroaki
    Kurosaki, Ken
    Fukumoto, Ken-ichi
    Yamanaka, Shinsuke
    JOURNAL OF NUCLEAR SCIENCE AND TECHNOLOGY, 2017, 54 (11) : 1267 - 1273
  • [26] Fracture toughness of Al2O3/ZrSiO4 coatings obtained by multi-chamber gas-dynamic accelerator
    Arseenko, M. Yu
    Kovaleva, M. G.
    Prozorova, M. S.
    Vagina, O. N.
    Yapryntsev, M. N.
    13TH INTERNATIONAL CONFERENCE ON FILMS AND COATINGS, 2017, 857
  • [27] Ageing behavior of Al–4.5 wt% Cu matrix alloy reinforced with Al2O3 and ZrSiO4 particulate varying particle size
    Sanjeev Das
    S. Das
    K. Das
    Journal of Materials Science, 2006, 41 : 5402 - 5406
  • [28] Sintering temperature depression in Al2O3 by mechanical milling
    Goodshaw, H. J.
    Forrester, J. S.
    Suaning, G. J.
    Kisi, E. H.
    JOURNAL OF MATERIALS SCIENCE, 2007, 42 (01) : 337 - 345
  • [29] Sintering temperature depression in Al2O3 by mechanical milling
    H. J. Goodshaw
    J. S. Forrester
    G. J. Suaning
    E. H. Kisi
    Journal of Materials Science, 2007, 42 : 337 - 345
  • [30] Reaction-sintering mechanisms of zirconia-mullite multiphase ceramics prepared from ZrSiO4/α-Al2O3 mixtures
    Zhao, SK
    Huang, XX
    Guo, JK
    JOURNAL OF INORGANIC MATERIALS, 2000, 15 (06) : 1102 - 1106
12345