DISSOLUTION OF ZRSIO4 AFTER MECHANICAL MILLING WITH AL2O3

被引：17
|
作者：
PUCLIN, T
KACZMAREK, WA
NINHAM, BW
机构：
[1] Institute of Advanced Studies, Research School of Physical Sciences and Engineering, The Australian National University, Canberra
来源：
MATERIALS CHEMISTRY AND PHYSICS | 1995年 / 40卷 / 02期
关键词：
ZIRCON DECOMPOSITION; MECHANOCHEMICAL PROCESSING; MECHANICAL MILLING;
D O I：
10.1016/0254-0584(94)01459-T
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A mixture of alumina (Al2O3) and zircon (ZrSiO4) was subjected to mechanical milling. The presence of alumina was found to greatly enhance the disordering of zircon. Acid leaching of the milled oxide mixtures resulted in complete dissolution of the zirconium, along with a proportion of alumina and only traces of silica. Zirconium leaching was not possible with zircon milled alone. Quantitative results of the leaching process are given.
引用
收藏
页码：105 / 109
页数：5
相关论文
共 50 条
  • [1] Effects of mechanical alloying on the reaction sintering of ZrSiO4 and Al2O3
    Khor, K.A.
    Li, Y.
    Materials Science and Engineering A, 1998, A256 (1-2): : 271 - 279
  • [2] Effects of mechanical alloying on the reaction sintering of ZrSiO4 and Al2O3
    Khor, KA
    Li, Y
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 256 (1-2): : 271 - 279
  • [3] Sinterability of ZrSiO4/α-Al2O3 mixed powders
    Zhao, SK
    Huang, Y
    Wang, CA
    Huang, XX
    Guo, JK
    CERAMICS INTERNATIONAL, 2003, 29 (01) : 49 - 53
  • [4] Mechanical properties of the plasma-sprayed Al2O3/ZrSiO4 coatings
    Li, Y
    Khor, KA
    SURFACE & COATINGS TECHNOLOGY, 2002, 150 (2-3): : 143 - 150
  • [5] The effect of residual stress on mechanical resistance of ZrSiO4/Al2O3 laminates
    Leon-Carriedo, Monica
    Alberto Gutierrez, Carlos
    Lopez-Cuevas, Jorge
    Ignacio Pech-Canul, Martin
    Luis Rodriguez-Galicia, Jose
    BOLETIN DE LA SOCIEDAD ESPANOLA DE CERAMICA Y VIDRIO, 2016, 55 (03): : 87 - 94
  • [6] Effect of interfacial diffusion on structural, physical, and mechanical properties of ZrSiO4/Al2O3 composites
    Murti, C. F. K.
    Sudiro, T.
    Zainuri, M.
    Endarko, E.
    Triwikantoro, T.
    MATERIALS CHEMISTRY AND PHYSICS, 2025, 333
  • [7] ZrSiO4 toughed Al2O3 ceramics prepared by reaction sintering
    Zheng, JM
    Ding, XG
    Chen, BJ
    Yang, H
    RARE METAL MATERIALS AND ENGINEERING, 2005, 34 : 405 - 408
  • [8] Mullite formation from reaction sintering of ZrSiO4/α-Al2O3 mixtures
    Zhao, SK
    Huang, Y
    Wang, CA
    Huang, XX
    Guo, JK
    MATERIALS LETTERS, 2003, 57 (11) : 1716 - 1722
  • [9] 海藻酸钠稳定Al2O3—ZrSiO4注浆料的研究
    张旭东
    何文
    张秀平
    中国陶瓷, 1994, (05) : 25 - 28
  • [10] Microstructure and composition analysis in plasma sprayed coatings of Al2O3/ZrSiO4 mixtures
    Li, Y
    Khor, KA
    SURFACE & COATINGS TECHNOLOGY, 2002, 150 (2-3): : 125 - 132
12345