Ni2P/ZrO2-SBA-15 Dibenzothiophene Hydrodesulfurization Catalysts: Preparation, Characterization and Evaluation

被引：3

作者：

Ma H. ^{[1
]}

Li Q. ^{[1
]}

Shi Y. ^{[1
]}

Sun X. ^{[1
]}

机构：

[1] School of Chemical Engineering and Technology, Tianjin University, Tianjin

来源：

Transactions of Tianjin University | 2018年 / 24卷 / 04期

关键词：

Hydrodesulfurization; Nickel phosphide; ZrO[!sub]2[!/sub] modified SBA-15;

D O I：

10.1007/s12209-017-0099-1

中图分类号：

学科分类号：

摘要：

Ni2P/ZrO2-SBA-15 catalysts with different zirconium n-propoxide/SBA-15 mass ratios were synthesized to evaluate their dibenzothiophene hydrodesulfurization catalytic activity. Effect of ZrO2 introduction was investigated. Supports and catalysts were characterized by BET, XRD, 29Si NMR, XPS and FTIR. The results indicated that zirconium was incorporated into SBA-15 in the forms of [(–O–)2Si(–O–Zr)2] and/or [(–O–)3Si–O–Zr], and that the SBA-15 framework structure was maintained after incorporation of ZrO2. With zirconium content increasing, ZrO2 was transformed from amorphous phase to tetragonal phase. Zirconium incorporation into SBA-15 supports could facilitate to form more dispersed Ni2P active phase. There might be some interaction occurring between the P and Zr species. In addition to Ni2P, another kind of active phase, ZrP, was formed, which might exhibit a better HDS activity than Ni2P. It was observed that at a temperature of 280 °C, pressure of 3.0 MPa, WHSV of 6.5 h−1 and H2 to oil ratio of 450, the Ni2P/Zr-SBA(1.5) catalyst, where 1.5 represents zirconium n-propoxide/SBA-15 mass ratio, showed the highest DBT conversion, which was 86.6%, almost 35% higher than that of the Ni2P/Zr-SBA(0) catalyst. © 2017, Tianjin University and Springer-Verlag GmbH Germany.

引用

页码：340 / 350

页数：10

共 48 条

[41]

Brunet E., Colon J.L., Clearfield A., Tailored organic-inorganic materials, (2015)

[42]

Guittet M.J., Crocombette J.P., Gautier-Soyer M., Bonding and XPS chemical shifts in ZrSiO4 versus SiO2 and ZrO2: charge transfer and electrostatic effects, Phys Rev B, 63, 12, (2001)

[43]

Fu J., Zheng P., Du P., Et al., Zirconium modified TUD-1 mesoporous catalysts for the hydrodesulfurization of FCC diesel, Appl Catal A, 502, pp. 320-328, (2015)

[44]

Fu W., Zhang L., Wu D., Et al., Mesoporous zeolite ZSM-5 supported Ni2P catalysts with high activity in the hydrogenation of phenanthrene and 4, 6-dimethyldibenzothiophene, Ind Eng Chem Res, 55, 26, pp. 7085-7095, (2016)

[45]

Chen T., Yang B., Li S., Et al., Ni2P catalysts supported on titania-modified alumina for the hydrodesulfurization of dibenzothiophene, Ind Eng Chem Res, 50, 19, pp. 11043-11048, (2011)

[46]

El Haskouri J., Cabrera S., Guillem C., Et al., Atrane precursors in the one-pot surfactant-assisted synthesis of high zirconium content porous silicas, Chem Mater, 14, 12, pp. 5015-5022, (2002)

[47]

Wang L., Wu X.L., Xu W.H., Et al., Stable organic-inorganic hybrid of polyaniline/α-zirconium phosphate for efficient removal of organic pollutants in water environment, ACS Appl Mater Interfaces, 4, 5, pp. 2686-2692, (2012)

[48]

Liu Q.Y., Liao Y.H., Wang T.J., Et al., One-pot transformation of cellulose to sugar alcohols over acidic metal phosphates combined with Ru/C, Ind Eng Chem Res, 53, 32, pp. 12655-12664, (2014)

← 1 2 3 4 5 →