Thermal oxidation behaviors and structures of Fe-9Cr-1Mo alloy

被引：0
作者：
J. D. Betancur
G. A. Pérez Alcazar
K. Nomura
C. J. Wang
J. A. Tabares
机构：
[1] Escuela Colombiana de Ingeniería Julio Garavito,Departamento de Ciencias Naturales
[2] Universidad del Valle,Departamento de Ciencias Naturales
[3] Tokyo University of Science,Department of Mechanical Engineering
[4] National Taiwan University of Science and Technology,undefined
来源：
Hyperfine Interactions | 2017年 / 238卷
关键词：
Isothermal oxidation; Fe-9Cr-1Mo alloy; CEMS; Mössbauer spectroscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Isothermal oxidation behaviors of Fe-9Cr-1Mo alloy were investigated at 600, 700, 750 and 850 ∘C for 72 h in air atmosphere. The oxidation rates were measured using a thermogravimetric analyzer (TGA). The structure and composition of the oxide scale were characterized by X-ray diffraction (XRD), energy dispersive spectrometry (EDS) and conversion electron Mössbauer spectrometry (CEMS). In this study it was found that the oxide layers form duplex structures consisting of Fe and Cr oxides. CEMS spectra are composed of one doublet due to dispersed Fe 3+ in Cr2O3 oxidation layers produced at high temperatures and two magnetic components due to Fe-Cr-Mo alloy substrate and hematite (Fe, Cr)2O3 with lower hyperfine field than pure hematite (52 T). Fe rich oxides are formed at the surface by oxidation at relatively low temperatures of 600 ∘C and 700 ∘C, while Cr rich (Fe, Cr)-oxides are formed in the top surface layers by oxidation at higher than 750 ∘C.
引用
收藏
相关论文
共 39 条
  • [1] Zhang Y(2004)undefined Oxid. Met. 62 103-132
  • [2] Pint BA(2001)undefined J. Nucl. Mater. 288 202-1004
  • [3] Haynes JA(2016)undefined Corros. Sci. 105 120-1740
  • [4] Tortorelli PF(2000)undefined Corros. Sci. 42 991-68
  • [5] Hong SG(2000)undefined Corros. Sci. 42 1725-1264
  • [6] Lee WB(2014)undefined Corros. Sci. 79 59-301
  • [7] Park CG(2004)undefined Spectrochim. Acta Part B 59 1259-780
  • [8] Rouillard F(2007)undefined Acta Metall. Slovaca 13 298-372
  • [9] Furukawa T(2001)undefined Czech. J. Phys. 51 773-undefined
  • [10] Greeff AP(2011)undefined Ingeniería y Univ. 15 359-undefined
1234