Spatial distribution of the increased porosity of cement paste due to calcium leaching

被引：0
作者：
Keshu Wan
Lin Li
Qiong Xu
Wei Sun
机构：
[1] Southeast University,Jiangsu Key Laboratory of Construction Materials, School of Materials Science and Engineering
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2015年 / 30卷
关键词：
calcium leaching; cement paste; characterization; increased porosity;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Using the tomography image, a method to characterize the 3D spatial distributions of increased porosity was proposed, and the increased porosity distributions of cement pastes with different leaching degrees were given using the current method. The leaching processes of CH/C-S-H and the contribution of CH/C-S-H leaching to porosity evolution were discussed. The proposed method can be applied to all cement-based materials with any leaching degrees. From the quantitative increased porosity results, we find that the CH leaching finished quickly on the sharp CH leaching front
引用
收藏
页码：735 / 744
页数：9
相关论文
共 50 条
  • [31] Mechanical tensile behaviour of cement paste/aggregate bond exposed to leaching
    Girboveanu, Andrei
    Jebli, Mouad
    Jamin, Frederic
    Huon, Vincent
    Bonnet, Laurent
    Georgescu, Dan
    El Youssoufi, Moulay Said
    CONSTRUCTION AND BUILDING MATERIALS, 2023, 369
  • [32] NANOINDENTATION AND POROSITY FRACTAL DIMENSION OF CALCIUM CARBONATE WHISKER REINFORCED CEMENT PASTE AFTER ELEVATED TEMPERATURES (UP TO 900°C)
    Li, Li
    Li, Zongli
    Cao, Mingli
    Tang, Yi
    Zhang, Zhe
    FRACTALS-COMPLEX GEOMETRY PATTERNS AND SCALING IN NATURE AND SOCIETY, 2021, 29 (02)
  • [33] Changes in mechanical performance and pore structure of hardened cement paste under the combined effect of calcium leaching and dry/wet cycles
    Di, Hongfeng
    Guan, Xuemao
    Liu, Songhui
    CONSTRUCTION AND BUILDING MATERIALS, 2023, 407
  • [34] Influence of Cement Particle Size Distribution on Strength of Hardened Cement Paste
    Zhu Baolin
    Huang Xin
    Guo Ye
    ECOLOGICAL ENVIRONMENT AND TECHNOLOGY OF CONCRETE, 2011, 477 : 118 - 124
  • [35] Long-term performance of cement paste during combined calcium leaching-sulfate attack: kinetics and size effect
    Planel, D
    Sercombe, J
    Le Bescop, P
    Adenot, F
    Torrenti, JM
    CEMENT AND CONCRETE RESEARCH, 2006, 36 (01) : 137 - 143
  • [36] A microstructure-based constitutive model for cement paste with chemical leaching effect
    Shen, W. Q.
    Shao, J. F.
    Burlion, N.
    Liu, Z. B.
    MECHANICS OF MATERIALS, 2020, 150 (150)
  • [37] Development of porosity of cement paste blended with supplementary cementitious materials after carbonation
    Wu, B.
    Ye, G.
    CONSTRUCTION AND BUILDING MATERIALS, 2017, 145 : 52 - 61
  • [38] Effect of carbonation on nitrite ion distribution in cement paste
    Li X.-Z.
    Liu J.-Z.
    Dai Y.-H.
    He Z.-M.
    Ba M.-F.
    Li Y.-S.
    Jilin Daxue Xuebao (Gongxueban)/Journal of Jilin University (Engineering and Technology Edition), 2019, 49 (04): : 1162 - 1168
  • [39] Effect of Vibration Procedure on Particle Distribution of Cement Paste
    Ke, Jia
    Shui, Zhonghe
    Gao, Xu
    Qi, Xibo
    Zheng, Zihang
    Zhang, Shaolin
    MATERIALS, 2023, 16 (07)
  • [40] Determination of Calcium Ions in Hydrated Cement Paste at Early Stage
    Hoskova, S.
    Ticha, P.
    Demo, P.
    ADVANCED MATERIALS FORUM V, PT 1 AND 2, 2010, 636-637 : 1239 - 1243
12345