Restoration of the microstructure of Ba2YCu3O7 − δ at T > 900°C after low-temperature decomposition

被引：0
作者：
I. B. Bobylev
E. I. Kuznetsova
T. P. Krinitsina
N. A. Zyuzeva
S. V. Sudareva
E. P. Romanov
机构：
[1] Russian Academy of Sciences,Institute of Metal Physics, Ural Branch
来源：
The Physics of Metals and Metallography | 2011年 / 112卷
关键词：
low-temperature decomposition; structure defects; pinning centers; critical current density;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Transmission electron microscopy and optical microscopy have been used to study the structure of the nonstoichiometric YBa2Cu3O7 − δ compound subjected to low-temperature annealing (200–300°C) and subsequent restoration annealing at 930–950°C. It was shown that the retention of part of structural defects, which were formed during decomposition and interaction with water vapor, after restoration annealing determines structural state of the compound that is typical of materials exhibiting improved electrophysical characteristics.
引用
收藏
页码：165 / 169
页数：4
相关论文
共 36 条
  • [1] Restoration of the Microstructure of Ba2YCu3O7-δ at T > 900°C after Low-Temperature Decomposition
    Bobylev, I. B.
    Kuznetsova, E. I.
    Krinitsina, T. P.
    Zyuzeva, N. A.
    Sudareva, S. V.
    Romanov, E. P.
    PHYSICS OF METALS AND METALLOGRAPHY, 2011, 112 (02) : 165 - 169
  • [2] NITROGEN-ION IRRADIATION EFFECT ON BA2YCU3O7 SUPERCONDUCTOR
    SHIRAISHI, K
    ITOH, H
    AOKI, Y
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1991, 30 (1A): : L25 - L27
  • [3] Microstructure of YBa2Cu3O6.8 after low-temperature annealing and subsequent restoration
    Kuznetsova, E. I.
    Krinitsina, T. P.
    Bobylev, I. B.
    Zyuzeva, N. A.
    Romanov, E. P.
    PHYSICS OF METALS AND METALLOGRAPHY, 2014, 115 (08) : 793 - 799
  • [4] Microstructure of YBa2Cu3O6.8 after low-temperature annealing and subsequent restoration
    E. I. Kuznetsova
    T. P. Krinitsina
    I. B. Bobylev
    N. A. Zyuzeva
    E. P. Romanov
    The Physics of Metals and Metallography, 2014, 115 : 793 - 799
  • [5] Electrophysical properties and the structure of the YBa2Cu3O y compound thermally restored after low-temperature decomposition
    Bobylev, I. B.
    Zyuzeva, N. A.
    Romanov, E. P.
    PHYSICS OF THE SOLID STATE, 2010, 52 (07) : 1338 - 1341
  • [6] DEPENDENCE OF CRITICAL CURRENT-DENSITY ON MICROSTRUCTURE IN AG SHEATHED BA2YCU3O6+X TAPES
    OSAMURA, K
    TAKAYAMA, T
    OCHIAI, S
    CRYOGENICS, 1990, 30 (05) : 430 - 433
  • [7] Influence of Growth Temperature on Microstructure and Superconducting Properties of ErBa2Cu3O7-δ Films With Ba(Er0.5Nb0.5)O3 Nanorods
    Kai, Hideki
    Horii, S.
    Ichinose, A.
    Yamada, K.
    Kita, R.
    Mukaida, M.
    Teranishi, R.
    Mori, N.
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2009, 19 (03) : 3435 - 3438
  • [8] Study synthesis of ( La1-xGdx) Ba2Cu3O7-δ superconductors at low temperature
    Sumadiyasa, M.
    Adnyana, I. G. A. Putra
    Widagda, I. G. A.
    Suharta, W. G.
    2016 INTERNATIONAL CONGRESS ON THEORETICAL AND APPLIED MATHEMATICS, PHYSICS AND CHEMISTRY, 2016, 725
  • [9] Electrophysical properties and the structure of the YBa2Cu3Oy compound thermally restored after low-temperature decomposition
    I. B. Bobylev
    N. A. Zyuzeva
    E. P. Romanov
    Physics of the Solid State, 2010, 52 : 1338 - 1341
  • [10] CHANGES OF SUPERCONDUCTIVITY AND CRYSTAL-STRUCTURE ON BA2YCU3O7-X BY 1 MEV AR+ ION IRRADIATION
    TERAI, T
    FURUTA, T
    MASEGI, T
    KUSAGAYA, K
    TAKAHASHI, Y
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1991, 30 (4B): : L728 - L731
1234