The effect of Bi4Ti3O12 particles addition in lead-free Bi0.5(Na0.75K0.25)0.5TiO3 ceramics

We studied the effect of Bi4Ti3O12 (BiT) platelet addition in Bi0.5(Na0.75K0.25)0.5TiO3 (BNKT) ceramics by preparing two kinds of BNKT ceramics. One type of BNKT ceramic was fabricated by a conventional solid state reaction method (normal sample), while the other by addition of 15 wt% BiT platelets to BNKT powders (BiT-added sample). In the case of BiT-added BNKT ceramics, plate like grains were formed by the reaction of BiT platelets with Na2CO3, K2CO3, and TiO2 during the sintering process. The grain size of BiT-added BNKT ceramics was 10 times larger than that of normal BNKT ceramic. The piezoelectric strain and d33 values of BiT-added BNKT ceramics were 0.135% and 225 pm/V, respectively. These values were 35% higher than those of normal BNKT ceramics. The piezoelectric properties of BiT-added BNKT ceramics were enhanced by the higher domain activity due to a decrease in domain density at larger grain sizes.