Cavitation erosion of NiAl

被引：0
作者：
A. Akhtar
R. Salvi
V. K. Sikka
机构：
[1] Powertech Labs Inc.,Metals and Materials Engineering Department
[2] University of British Columbia,Metals and Materials Engineering Department
[3] University of British Columbia,the Metals and Ceramics Division
[4] Soligen Technologies Inc.,undefined
[5] Oak Ridge National Laboratory,undefined
来源：
Metallurgical and Materials Transactions A | 1999年 / 30卷
关键词：
Martensite; Cavitation; Material Transaction; Erosion Rate; NiAl;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Vibratory cavitation erosion tests were carried out on as-cast NiAl intermetallic compounds containing 46.5 to 62.1 at pct Ni. The erosion rate decreased with increasing nickel content by over two orders of magnitude, from a high of 16.4 to 0.11 mg·h−1. These low erosion rates exhibited by the nickel-rich alloys containing 58 and 62.1 at. pct Ni, the interruptions in their mass loss with time, and the unusual effects associated with surface finish and intensity of cavitation were found to be associated with the stress-induced martensitic transformation. Alloys containing 58 to 62 at. pct Ni have the potential for use as materials for the cavitation protection of hydraulic machinery.
引用
收藏
页码：335 / 343
页数：8
相关论文
共 50 条
[1]   Cavitation erosion of NiAl-bronze layers generated by friction surfacing [J].
Hanke, Stefanie ;
Fischer, Alfons ;
Beyer, Matthias ;
dos Santos, Jorge .
WEAR, 2011, 273 (01) :32-37
[2]   Cavitation erosion characteristics of a NiTi alloy [J].
W. Liu ;
Y. G. Zheng ;
Z. M. Yao ;
C. S. Liu .
Metallurgical and Materials Transactions A, 2004, 35 :356-362
[3]   Review on Cavitation Erosion Tests and Cavitation Erosion-resistant Materials [J].
Yang, Rui ;
Tian, Ye ;
Liu, Yi ;
Li, Hua .
Zhongguo Biaomian Gongcheng/China Surface Engineering, 2024, 37 (06) :164-204
[4]   Cavitation erosion of aluminas [J].
Tomlinson, W ;
Kalitsounakis, N ;
Vekinis, G .
CERAMICS INTERNATIONAL, 1999, 25 (04) :331-338
[5]   Simultaneous observation of cavitation structures and cavitation erosion [J].
Petkovsek, Martin ;
Dular, Matevz .
WEAR, 2013, 300 (1-2) :55-64
[6]   Cavitation erosion and surface modification using cavitation [J].
Soyama, H .
JOURNAL OF JAPANESE SOCIETY OF TRIBOLOGISTS, 2003, 48 (10) :814-820
[7]   Pit clustering in cavitation erosion [J].
Dular, Matevz ;
Osterman, Aljaz .
WEAR, 2008, 265 (5-6) :811-820
[8]   Development of a cavitation erosion model [J].
Dular, Matevz ;
Stoffel, Bernd ;
Sirok, Brane .
WEAR, 2006, 261 (5-6) :642-655
[9]   Cavitation erosion of bainitic steel [J].
Jiang, GB ;
Zheng, YK ;
Yang, YY ;
Fang, HS .
WEAR, 1998, 215 (1-2) :46-53
[10]   Cavitation erosion of copper and copper-based alloys [J].
Hucinska, J ;
Glowacka, M .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (06) :1325-1333
12345