Performance of a Steam Pipeline with Defects in Knot Welded Joints

被引：0

作者：

Grin’ E.A. ^{[1
]}

Zelenskii A.V. ^{[1
]}

机构：

[1] All-Russia Thermal Engineering Institute JSC, Moscow

来源：

Power Technology and Engineering | 2021年 / 54卷 / 5期

关键词：

allowable crack size; allowable service life; brittle strength; control; crack-like defect; steam pipeline; stress; stress intensity factor; welded joint;

D O I：

10.1007/s10749-020-01275-y

中图分类号：

学科分类号：

摘要：

The analysis of the possibility of temporary operation of a steam pipeline with defects in knot welded joints was performed on a specific example. Based on the conservative approach, the tensile stresses in the working sections of the pipeline were determined and the stress intensity factors for crack-like defects oriented in the circumferential direction along the knot joints were calculated. It is shown that the loss of the bearing capacity of the pipeline with defects by the mechanism of exhaustion of brittle strength is excluded. The allowable sizes of crack-like defects in the zones of welded joints were determined by calculation based on the characteristics of plastic limiting states. Using a special technique, the time period of temporary safe operation of a pipeline with crack-like defects until it was taken out for repair was calculated. © 2021, Springer Science+Business Media, LLC, part of Springer Nature.

引用

页码：714 / 719

页数：5

共 13 条

[1]

RD 10-577–03, Typical Instruction for Metal Control and Extension of the Service Life of the Main Elements of Boilers, Turbines and Pipelines of Thermal Power Plants [In Russian], (2004)

[2]

Main Elements of Boilers, Turbines and Pipelines of Tpps. Metal Condition Monitoring, (2008)

[3]

Industrial Safety Rules for Hazardous Production Facilities Using Equipment Operating under Excessive Pressure [In Russian], (2014)

[4]

General Requirements for the Safety Substantiation of a Hazardous Industrial Facility [In Russian], (2013)

[5]

Standards for Calculating the Strength of Stationary Boilers and Pipelines of Steam and Hot Water, GUP Nauchno-Tekhnicheskii Tsentr Po Bezopasnosti V Promyshlennosti Gosgortekhnadzora Rossii, (2002)

[6]

Grin E.A., Anokhov A.E.

[7]

Calculation of Stress Intensity Factors [In Russian], (1986)

[8]

Standards for Calculating the Strength of Equipment and Pipelines of Nuclear Power Plants, (1989)

[9]

Kogaev V.P., Makhutov N.A., Gusenkov A.P., Strength and Durability Calculations of Machine Parts and Structures [in Russian], (1985)

[10]

Technique for Predicting the Residual Life of Power Equipment Elements Based on the Results of Their Operational Control: Report of the All-Russia Thermal Engineering Institute, (1988)

← 1 2 →