Calcium phosphate based ceramic with a resorbable phase and low sintering temperature

被引：0

作者：

M. N. Safina

T. V. Safronova

E. S. Lukin

机构：

[1] D. I. Mendeleev Russian Chemical Engineering University,

[2] M. V. Lomonosov Moscow State University,undefined

来源：

Glass and Ceramics | 2007年 / 64卷

关键词：

Calcination Temperature; Flexural Strength; Calcium Phosphate; Open Porosity; Eutectic Composition;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The use of glasses with eutectic compositions in the system CaO-P2O5 as a sintering aid and as a source of a resorbable phase for obtaining a composite biomaterial for bone implants is examined. The use of such glass has made it possible not only to lower the sintering temperature by realization of the mechanism of liquid-phase sintering but also to form a ceramic material possessing bioresorbability. The material obtained consists of calcium hydroxyapatite, vitlokite, and calcium pyrophosphate phases.

引用

页码：238 / 243

页数：5

共 26 条

[1]

Putlyaev V. I.(2005)New generation of calcium phosphate biomaterials: role of phase and chemical composition Steklo Keram. 3 30-33

[2]

Safronova T. V.(2003)Phosphate based glasses for biomedical applications J. Mater. Chem. 13 2395-2401

[3]

Knowles J. C.(2007)A new rhenanite (β-NaCaPO J. Biomed. Mater. Res., Part B: Appl. Biomater. 80B 304-316

[4]

Jalota S.(2005)) and hydroxyapatite biphasic biomaterial for skeletal repair J. Am. Ceram. Soc. 88 3096-3103

[5]

Bhaduri S. B.(2002)Cement formulations in the calcium phosphate H Biomaterials 23 1065-1072

[6]

Tas A. C.(2007)O-H Neorg. Mater. 8 1-10

[7]

Grover L. M.(2005)PO J. Ceram. Soc. Jpn. 113 669-673

[8]

Gbureck U.(2006)-H Konstr. Kompozit. Mater. 4 39-43

[9]

Wright A. J.(2000)P Steklo Keram. 1 22-24

[10]

Barrale J. E.(undefined)O undefined undefined undefined-undefined

← 1 2 3 →