Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates Under Different Loading Rates Using Acoustic Emission

被引：0
作者：
D. Xu
P. F. Liu
Z. P. Chen
J. G. Li
J. X. Leng
R. H. Zhu
L. Jiao
J. Mu
Y. Y. Li
L. L. Wang
机构：
[1] Zhejiang University,Institute of Chemical Machinery and Process Equipment, School of Energy Engineering
[2] Zhejiang University,Ocean College
来源：
Journal of Failure Analysis and Prevention | 2019年 / 19卷
关键词：
Delamination analysis; Loading rate effects; Carbon fiber/epoxy composite laminates; Single-leg three-point bending tests; Acoustic emission;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This work studies delamination behaviors of carbon fiber/epoxy composite laminates under different loading rates using acoustic emission (AE) that shows large advantage for dynamic monitoring of instantaneous defects by analyzing characteristic signal parameters. Generally, rate-dependent damage behaviors of composites poses challenges to AE signal analysis and failure mode identification during a short time. In order to study dynamic mixed-mode delamination behaviors, the single-leg three-point bending tests for carbon fiber/epoxy composite laminates with initial intralaminar and interlaminar truncation sizes under different loading rates are performed. Effects of the loading rate and layup pattern on the delamination behaviors of composites are studied by analyzing the AE responses including the amplitude and energy.
引用
收藏
页码：1034 / 1042
页数：8
相关论文
共 62 条
  • [1] Liu PF(2017)Delamination analysis of carbon fiber composites under hygrothermal environment using acoustic emission J. Compos. Mater. 51 1557-1571
  • [2] Yang J(2012)A study on the failure mechanisms of carbon fiber/epoxy composite laminates using acoustic emission Mater. Des. 37 228-235
  • [3] Peng XQ(1999)Initiation and growth of delamination in glass/epoxy composites subjected to static and dynamic loading by acoustic emission monitoring Compos. Sci. Technol. 59 201-208
  • [4] Liu PF(2011)Monitoring the initiation and growth of delamination in composite materials using acoustic emission under quasi-static three-point bending test J. Reinf. Plast. Compos. 30 1481-1493
  • [5] Chu JK(2013)Acoustic emission monitoring of interlaminar delamination onset in carbon fiber composites Struct. Health Monit. 12 126-140
  • [6] Liu YL(2016)Prediction of quasi-static delamination onset and growth in laminated composites by acoustic emission Compos. Part B Eng. 85 113-122
  • [7] Benmedakhene S(2010)Quantitative experimental measurements of matrix cracking and delamination using acoustic emission Compos. Part A Appl. Sci. Manuf. 41 612-623
  • [8] Kenane M(2015)Localisation and identification of fatigue matrix cracking and delamination in a carbon fibre panel by acoustic emission Compos. Part B Eng. 74 1-12
  • [9] Benzeggagh ML(2017)Delamination evaluation of composite laminates with different interface fiber orientations using acoustic emission features and micro visualization Compos. Part B Eng. 113 185-196
  • [10] Fotouhi M(2015)Prediction of delamination growth in laminated composites using acoustic emission and cohesive zone modeling techniques Compos. Struct. 124 120-127
1234567