Nano Brazing of Pt-Ag Nanoparticles under Femtosecond Laser Irradiation

被引：0
作者：
L. Liu
H. Huang
A. Hu
G. Zou
L. Quintino
Y. Zhou
机构：
[1] Tsinghua University,Department of Mechanical Engineering
[2] University of Waterloo,Department of Mechanical & Mechatronics Engineering
[3] Technical University of Lisbon,undefined
来源：
Nano-Micro Letters | 2013年 / 5卷 / 2期
关键词：
Femtosecond laser; Nanojoining; Nanoparticles;
D O I：
10.1007/BF03353734
中图分类号：
学科分类号：
摘要：
Nano brazing of Pt-Ag nanoparticles with nano Ag filler metal is reported in this letter, which presents an effective way to join nanoobjects by femtosecond laser irradiation. The nano brazed interface between Pt-Ag and Ag showed good lattice matching along (111)Ag//(111)Ag-Pt. Lattice mismatch can hardly be observed at the interface between the filler metal and Pt-Ag nanoparticle, which is important for the joint strength and normally does not occur during joining. The very low mismatch also suggested that melting and solidification occurred during nano brazing by femtosecond laser. The role of Brownian motion on the nano joining process is also discussed in this paper.
引用
收藏
页码：88 / 92
页数：4
相关论文
共 70 条
  • [31] Kabashin A V(undefined)undefined undefined undefined undefined-undefined
  • [32] Meunier M(undefined)undefined undefined undefined undefined-undefined
  • [33] Zhang J(undefined)undefined undefined undefined undefined-undefined
  • [34] Worley J(undefined)undefined undefined undefined undefined-undefined
  • [35] Denommee S(undefined)undefined undefined undefined undefined-undefined
  • [36] Kingston C(undefined)undefined undefined undefined undefined-undefined
  • [37] Jakubek Z J(undefined)undefined undefined undefined undefined-undefined
  • [38] Deslandes Y(undefined)undefined undefined undefined undefined-undefined
  • [39] Post M(undefined)undefined undefined undefined undefined-undefined
  • [40] Simard B(undefined)undefined undefined undefined undefined-undefined
1234567