Suppression of discontinuous precipitation in AZ91 by addition of Sn

被引：1
作者：
I. C. Jung
Y. K. Kim
T. H. Cho
S. H. Oh
T. E. Kim
S. W. Shon
W. T. Kim
D. H. Kim
机构：
[1] Yonsei University,Department of Metallurgical Engineering
[2] Cheongju University,Applied Science Division
来源：
Metals and Materials International | 2014年 / 20卷
关键词：
alloy; solidification; aging; phase transformation; mechanical properties;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effect of Sn (5 wt%) addition on the aging behavior of the AZ91 alloy has been investigated in the present study. The addition of Sn effectively suppresses the discontinuous precipitation during aging treatment. The aging response of the Sn containing AZ91 alloy is far better than that of the AZ91 alloy due to much higher density of continuous precipitation in the matrix. The yield strength and total elongation to failure at the peak aged condition of the AZ91 and Sn containing AZ91 alloys are 119.4 and 161.9 MPa and 8.8 and 8.6%, respectively, indicating that 35.6% increase of yield strength can be obtained by the addition of Sn in the AZ91 alloy maintaining almost same level of ductility.
引用
收藏
页码：99 / 103
页数：4
相关论文
共 70 条
  • [1] Srinivasan A(2007)undefined Mater. Sci. Eng. A 452–453 87-undefined
  • [2] Pillai U T S(2002)undefined Met. Mater. Int. 8 551-undefined
  • [3] Pai B C(2003)undefined Mater. Sci. Eng. A 356 1-undefined
  • [4] Park S S(2001)undefined Mater. Sci. Eng. A 308 38-undefined
  • [5] Park Y S(1968)undefined Acta Metall. 16 141-undefined
  • [6] Kim N J(2001)undefined Int. Mater. Rev. 46 53-undefined
  • [7] Wenwen D(1994)undefined Acta Metall. Mater 43 101-undefined
  • [8] Yangshan S(2001)undefined Metall. Mater. Trans. A 32 787-undefined
  • [9] Dengym W(1994)undefined Acta Metall. 42 3843-undefined
  • [10] Guangyin Y(2011)undefined Mater. Sci. Eng. A 528 5018-undefined
1234567