Microstructure and Mechanical Properties of Fiber-Laser-Welded and Diode-Laser-Welded AZ31 Magnesium Alloy

被引:0
作者
S. M. Chowdhury
D. L. Chen
S. D. Bhole
E. Powidajko
D. C. Weckman
Y. Zhou
机构
[1] Ryerson University,Department of Mechanical and Industrial Engineering
[2] University of Waterloo,Department of Mechanical and Mechatronics Engineering
来源
Metallurgical and Materials Transactions A | 2011年 / 42卷
关键词
Welding; Base Metal; Fatigue Strength; Weld Pool; Fusion Zone;
D O I
暂无
中图分类号
学科分类号
摘要
The microstructures, tensile properties, strain hardening, and fatigue strength of fiber-laser-welded (FLW) and diode-laser-welded (DLW) AZ31B-H24 magnesium alloys were studied. Columnar dendrites near the fusion zone (FZ) boundary and equiaxed dendrites at the center of FZ, with divorced eutectic β-Mg17Al12 particles, were observed. The FLW joints had smaller dendrite cell sizes with a narrower FZ than the DLW joints. The heat-affected zone consisted of recrystallized grains. Although the DLW joints fractured at the center of FZ and exhibited lower yield strength (YS), ultimate tensile strength (UTS), and fatigue strength, the FLW joints failed at the fusion boundary and displayed only moderate reduction in the YS, UTS, and fatigue strength with a joint efficiency of ~91 pct. After welding, the strain rate sensitivity basically vanished, and the DLW joints exhibited higher strain-hardening capacity. Stage III hardening occurred after yielding in both base metal (BM) and welded samples. Dimple-like ductile fracture characteristics appeared in the BM, whereas some cleavage-like flat facets together with dimples and river marking were observed in the welded samples. Fatigue crack initiated from the specimen surface or near-surface defects, and crack propagation was characterized by the formation of fatigue striations along with secondary cracks.
引用
收藏
页码:1974 / 1989
页数:15
相关论文
共 184 条
[1]  
Pollock T.M.(2010)undefined Science 328 986-87
[2]  
Wise M.(2009)undefined Science 324 1183-86
[3]  
Calvin K.(2002)undefined Nature 419 188-90
[4]  
Thomson A.(2005)undefined Nature 438 310-17
[5]  
Clarke L.(2008)undefined Adv. Mater. Process. 166 35-37
[6]  
Bond-Lamberty B.(2004)undefined JOM 56 20-21
[7]  
Sands R.(1999)undefined J. Laser Appl. 11 273-78
[8]  
Smith S.J.(1998)undefined Metall. Mater. Trans. A 45A 1269-79
[9]  
Janetos A.(1985)undefined Metall. Trans. A 16A 1887-96
[10]  
Edmonds J.(1993)undefined Metall. Trans. A 24A 1433-46