Strengthening and Toughening of a Heavy Plate Steel for Shipbuilding with Yield Strength of Approximately 690 MPa

被引:0
作者
Dongsheng Liu
Binggui Cheng
Yuanyuan Chen
机构
[1] Institute of Research of Iron and Steel,
[2] Shasteel,undefined
[3] Jinfeng,undefined
来源
Metallurgical and Materials Transactions A | 2013年 / 44卷
关键词
Continuous Cool Transformation; Granular Bainite; Simulated HAZs; Heavy Plate; Charpy Versus Notch;
D O I
暂无
中图分类号
学科分类号
摘要
HSLA-100 steel with high content of alloying elements (nominally in wt pct, 3.5 Ni, 1.6 Cu, and 0.6Mo) is now used to produce heavy plates for constructing a hull and drilling platform. We proposed here a substantially leaner steel composition (containing 1.7 Ni, 1.1 Cu, and 0.5Mo) to produce a heavy plate to 80 mm thickness with mechanical properties comparable with those of the HSLA-100 grade. A continuous cooling transformation (CCT) diagram of the steel was constructed. Key parameters of thermal treatment and revealing mechanisms of strengthening and toughening were derived based on industrial production trials. The microstructures of the 80-mm-thick plate were lath-like bainite (LB) at near surface of the quarter thickness (t/4), and granular bainite (GB)+LB at center thickness (t/2) after solutionizing and water quenching (Q). The effect of tempering (T) on the microstructures and properties of the plate was investigated. Excellent combination of room temperature strength and low-temperature Charpy V-notch (CVN) toughness approximately equivalent to that of the HSLA 100 grade (YS > 690 MPa, CVN energy >100 J even at 193 K [−80 °C]) was achieved in the plate treated by the QT process with tempering temperature of 898 K (625 °C). The combination of strength and toughness at t/4 is superior to that at t/2 of the plate under both as-quenched and QT conditions. This result is attributed to that the fraction of high-angle grain boundaries (HAGBs) at t/4 is higher than that at t/2.
引用
收藏
页码:440 / 455
页数:15
相关论文
共 125 条
  • [1] DeArdo A.J.(1995)undefined ISIJ Int. 35 946-54
  • [2] Mujahid M.(1998)undefined J. Mater. Eng. Perform. 7 247-57
  • [3] Lis A.K.(1998)undefined Mater. Sci. Eng. A A252 256-68
  • [4] Garcia C.I.(2001)undefined Metall. Mater. Trans. A 32A 2259-70
  • [5] DeArdo A.J.(2004)undefined ISIJ Int. 44 115-22
  • [6] Hwang G.C.(2008)undefined Mater. Sci. Eng. A A486 152-57
  • [7] Lee S.(2003)undefined Metall. Mater. Trans. A 34A 1297-1309
  • [8] Yoo J.Y.(2006)undefined Metall. Mater. Trans. A 37A 2159-69
  • [9] Choo W.Y.(2003)undefined Metall. Mater. Trans. A 34A 2493-2504
  • [10] Dhua S.K.(2011)undefined Trans. Mater. Heat Treat. 32 125-35