Heat Resistance of Zr–1Nb Alloy Claddings in Water Vapor after Ion-Plasma Nitriding

被引：0

作者：

V. A. Zuyok

O. S. Kuprin

I. O. Klymenko

H. M. Tolmachova

M. V. Tretiakov

R. O. Rud

Ya.A. Kushtym

I. V. Dykyi

I. V. Shevchenko

V. V. Shtefan

机构：

[1] National Science Center “Kharkiv Institute of Physics and Technology”,National Academy of Sciences of Ukraine

[2] National Technical University “Kharkiv Polytechnic Institute”,Ministry of Education and Science of Ukraine

来源：

Materials Science | 2023年 / 58卷

关键词：

Zirconium alloy; Cladding; Ion-plasma nitriding; Oxidation; Water steam;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The influence of ion-plasma nitriding time of Zr–1Nb alloy fuel cladding tubes on their resistance to oxidation in water vapor at 600–1200°C was studied. The hardness of the samples along the wall thickness increases from 2 to 3 GPa, and on the surface up to 12 GPa depending on the processing time. The nitrided tubes oxidize much more under cracking and delamination of the oxide layer compared to the initial state.

引用

页码：548 / 553

页数：5

共 6 条

[1] Trush VS(2021)Influence of the functional layer on the operating characteristics of Zr–1% Nb alloy at a temperature of 380°C Mater. Sci. 57 234-239
[2] Fedirko VM(undefined)undefined undefined undefined undefined-undefined
[3] Lukyanenko AG(undefined)undefined undefined undefined undefined-undefined
[4] Voyevodin VM(undefined)undefined undefined undefined undefined-undefined
[5] Stoev PI(undefined)undefined undefined undefined undefined-undefined
[6] Panov VA(undefined)undefined undefined undefined undefined-undefined

← 1 →