Deformation characterization of superplastic AA7475 alloy

被引：0
|
作者：
P. Mukhopadhyay
S. Biswas
A. H. Chokshi
机构：
[1] Defence Institute of Advanced Technology,Material Science Department
[2] Indian Institute of Science,Materials Engineering Department
来源：
Transactions of the Indian Institute of Metals | 2009年 / 62卷
关键词：
superplastic deformation; recovery; recrystallization in-situ; CSL; high angle and low angle boundary;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
AA7475 alloy was deformed up to 25% elongation in INSTRON at 788K. The grain boundary sliding due to this superplastic deformation was measured by Scanning Electron Microscope. The microstructure and texture development due to this deformation at elevated temperature was analyzed from the Orientation Image Microstructures i.e. the Electron Back Scattered Diffraction Image. The Orientation Image Microstructures revealed that superplastic deformation was associated with recovery and recrystallization in-situ process.
引用
收藏
页码：149 / 152
页数：3
相关论文
共 50 条
  • [1] Deformation characterization of superplastic AA7475 alloy
    Mukhopadhyay, P.
    Biswas, S.
    Chokshi, A. H.
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2009, 62 (02) : 149 - 152
  • [2] Superplastic behavior of AA7475 aluminum alloy
    Zelin, MG
    Guillard, S
    Chaudhury, PK
    SUPERPLASTICITY IN ADVANCED MATERIALS - ICSAM-97, 1997, 243-2 : 137 - 142
  • [3] Superplastic behavior of AA7475 aluminum alloy
    Zelin, M.G.
    Guillard, S.
    Chaudhury, P.K.
    Materials Science Forum, 1997, 243-245 : 137 - 142
  • [4] Re-examination of "missing strain" during superplastic deformation of AA7475
    Tan, MJ
    Chen, CL
    Chandra, N
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 374 (1-2): : 369 - 373
  • [5] Comparison between superplastic deformation mechanisms at primary and steady stages of the fine grain AA7475 aluminium alloy
    Mikhaylovskaya, A. V.
    Yakovtseva, O. A.
    Sitkina, M. N.
    Kotov, A. D.
    Irzhak, A. V.
    Krymskiy, S. V.
    Portnoy, V. K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 718 : 277 - 286
  • [6] Theoretical prediction and FEM analysis of superplastic forming of AA7475 aluminum alloy in a hemispherical die
    Kumar, VSS
    Viswanathan, D
    Natarajan, S
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2006, 173 (03) : 247 - 251
  • [7] Grain boundary sliding during superplastic stretching of AA7475 cylindrical cups
    Zelin, MG
    JOURNAL OF MATERIALS SCIENCE, 1997, 32 (04) : 1075 - 1082
  • [8] Grain boundary sliding during superplastic stretching of AA7475 cylindrical cups
    M. G ZELIN
    Journal of Materials Science, 1997, 32 : 1075 - 1082
  • [9] On microsuperplasticity in AA7475 domes
    Zelin, MG
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (05): : 1400 - 1403
  • [10] An investigation of the hot deformation behavior of AA7020 and AA7475 aluminum alloys
    Ahmed, H.
    Eivani, A.
    Zhou, J.
    Duszczyk, J.
    ALUMINUM ALLOYS: FABRICATION, CHARACTERIZATION AND APPLICATIONS, 2008, : 33 - 40
12345