Infiltration Behavior of CMAS in LZ-YSZ Composite Thermal Barrier Coatings

被引：0
作者：
Guanlin Lyu
Dowon Song
Baig-Gyu Choi
Yeon-Gil Jung
机构：
[1] Changwon National University,School of Materials Science and Engineering
[2] Hanyang University,Department of Energy Engineering
[3] Korea Institute of Materials Science,High Temperature Materials Research Group
来源：
JOM | 2021年 / 73卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Calcium magnesium alumina-silicate (CMAS) corrosion on thermal barrier coatings (TBCs) is one of the reasons for the early delamination of TBCs. In this study, the effects of CMAS on the microstructure evolution of TBCs were investigated for yttria-stabilized zirconia (YSZ), lanthanum zirconate (LZ), and composite coating with a 50:50 volume ratio of LZ and YSZ (LZ-YSZ). The LZ showed the mitigated penetration of CMAS by the formation of the reaction products produced by the high reactivity between the LZ and the molten CMAS. The LZ-YSZ showed a denser microstructure on the surface, resulting in retarding the penetration of CMAS. Therefore, the LZ-YSZ composite TBC is expected to prolong the lifetime performance and protect against further corrosive degradation of TBCs in high-temperature environments. The infiltration behavior and reaction mechanism of molten CMAS were discussed based on the microstructures after the corrosion test.
引用
收藏
页码：541 / 550
页数：9
相关论文
共 222 条
[21]  
Bartsch M(2013)undefined Ceram. Int. 39 1413-undefined
[22]  
Baufeld B(2017)undefined Surf. Coat. Technol. 332 64-undefined
[23]  
Tikhonovsky A(2019)undefined Adv. Appl. Ceram. 118 257-undefined
[24]  
Foitzik A(2019)undefined J. Alloys Compd. 798 773-undefined
[25]  
Rühle M(2019)undefined J Mater. Today: Proc. 568 19-undefined
[26]  
Messerschmidt U(2017)undefined J. Mater. Lett. 108 191-undefined
[27]  
Vassen R(2006)undefined J. Am. Ceram. Soc. 89 3167-undefined
[28]  
Cao X(2002)undefined Science 296 280-undefined
[29]  
Tietz F(2015)undefined Surf. Coat. Technol. 268 298-undefined
[30]  
Basu D(2020)undefined Ceram. Int. 46 1307-undefined
12345678910