Fabrication and properties of novel composites in the system Al–Zr–C

Composite bodies in the system Al–Zr–C, with about 95% relative density, were obtained by heating the compact body of powder mixture consisting of Al and ZrC (5 : 1 mol %) in Ar at 1100–1500°C for various lengths of time. Components of the material heated at more than 1200°C were Al, Al3Zr, ZrC and AlZrC2. The Al3Zr exhibited plate-like aggregation, and its size increased with increasing temperature. In the material heated at 1500°C for 1 h, the largest plate-like Al3Zr aggregation was 2000 μm long and 133 μm thick. Then the AlZrC2 was present as well-proportioned hexagonal platelet particles with a 8–9 μm diameter and a 1–2 μm thickness in the interior of the plate-like Al3Zr aggregation and Al matrix phase. The average three-point bending strength of the bodies was 140–190 MPa, and the maximum strength was 203 MPa in the body heated at 1300°C for 1 h. The body heated at 1500°C for 1 h showed high oxidation resistivity to air up to 1000°C.