Mesoporous bimetallic Fe/Co as highly active heterogeneous Fenton catalyst for the degradation of tetracycline hydrochlorides

被引:0
作者
Junchao Li
Xuhua Li
Jindong Han
Fansheng Meng
Jinyuan Jiang
Jiao Li
Chunlian Xu
Yun Li
机构
[1] Chinese Research Academy of Environmental Sciences,State Key Laboratory of Environmental Criteria and Risk Assessment
来源
Scientific Reports | / 9卷
关键词
D O I
暂无
中图分类号
学科分类号
摘要
Mesoporous bimetallic Fe/Co was prepared as a Fenton-like catalyst to degrade the tetracycline hydrochlorides (TC). The nanocasting strategy with KIT-6 as a hard template was carried out to synthesize the mesoporous bimetallic catalyst. The mesoporous bimetallic Fe/Co catalyst was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), nitrogen adsorption-desorption isotherms, and Brunauer-Emmett-Teller (BET) method. The results showed that the catalyst has significant nanofeatures; the surface area, pore size, and particle size were 113.8 m2g−1, 4 nm, and 10 nm, respectively. In addition, the effects of the operating parameters, such as the iron-to-cobalt ratio, pH, H2O2, and initial TC concentrations on its catalytic performance were investigated. The best operating parameters were as follows: iron-to-cobalt ratio = 2:1 to 1:1, pH = 5–9, H2O2: 30 mmol, initial TC less than 30 mg/L. Furthermore, the mesoporous bimetallic Fe/Co showed a good performance for degrading TC, achieving a removal rate of 86% of TC after 3 h under the reaction conditions of H2O2 = 30 mmol, mesoporous bimetallic Fe/Co = 0.6 g/L, TC = 30 mg/L, pH = 7.0, and temperature = 25.5 °C. The mesoporous bimetallic Fe/Co catalyst shows good stability and reusability. This work demonstrated that mesoporous bimetallic Fe/Co has excellent catalytic efficiency, smaller amounts of leached ions, and wider pH range, which enhance its potential applications.
引用
收藏
相关论文
共 65 条
[1]  
Rizzo L(2013)Urban wastewater treatment plants as hotspots for the release of antibiotics in the environment: A review Water Res. 47 957-995
[2]  
Zhang QQ(2015)Comprehensive Evaluation of Antibiotics Emission and Fate in the River Basins of China: Source Analysis, Multimedia Modeling, and Linkage to Bacterial Resistance Environ. Sci. Technol. 49 6772-6782
[3]  
Kim S(2005)Removal of Antibiotics in Wastewater: Effect of Hydraulic and Solid Retention Times on the Fate of Tetracycline in the Activated Sludge Process Environ. Sci. Technol. 39 5816-5823
[4]  
Munoza M(2013)A ferromagnetic-alumina-supported iron catalyst for CWPO.Application to chlorophenols Appl. Catal. B: Environ. 136–137 218-224
[5]  
Su S(2013)Heterogeneous activation of Oxone by Co J Hazard Mater 244–245 736-742
[6]  
Al-Shamsi MA(2013)Fe Chem. Eng. J. 232 555-563
[7]  
Thomson NR(2016)O Sci. Rep. 6 1-10
[8]  
Forsey SP(2016) nanocatalysts for degradation of rhodamine B Sep. Purif. Technol. 171 80-87
[9]  
Qiu B(2016)Iron based bimetallic nanoparticles to activate peroxygens J. Eniron. Manage. 182 284-291
[10]  
Yu L(2012)Ultradispersed Cobalt Ferrite Nanoparticles Assembled in Graphene Aerogel for Continuous Photo-Fenton Reaction and Enhanced Lithium Storage Performance Chem. Eng. J. 191 356-363