Spalling of intermetallic compounds during the reaction between lead-free solders and electroless Ni-P metallization

被引:0
作者
Y. C. Sohn
Jin Yu
S. K. Kang
D. Y. Shih
T. Y. Lee
机构
[1] Korea Advanced Institute of Science and Technology,Department of Materials Science and Engineering
[2] IBM T.J. Watson Research Center,Department of Materials Science and Engineering
[3] Hanbat National University,undefined
来源
Journal of Materials Research | 2004年 / 19卷
关键词
D O I
暂无
中图分类号
学科分类号
摘要
Intermetallic compound (IMC) spalling from electroless Ni-P film was investigated with lead-free solders in terms of solder-deposition methods (electroplating, solder paste, and thin foil), P content in the Ni-P film (4.6, 9, and 13 wt% P), and solder thickness (120 versus .200 μm). The reaction of Ni-P with Sn3.5Ag paste easily led to IMC spalling after 2-min reflow at 250 °C while IMCs adhered to the Ni-P layer after 10-min reflow with electroplated Sn or Sn3.5Ag. It has been shown that not only the solder composition but also the deposition method is important for IMC spalling from the Ni-P layer. The spalling increased with P content as well as with solder volume. Ni3Sn4 intermetallics formed as a needle-shaped morphology at an early stage and changed into a chunk-shape. Needle-shaped compounds exhibited a higher propensity for spalling than chunk-shaped compounds because many channels among the needle-shaped IMCs facilitated Sn penetration. A reaction between the penetrated Sn and the Ni3P layer formed a Ni3SnP layer and Ni3Sn4 IMCs spalled off the Ni3SnP surface. Dewetting of solder from the Ni3SnP layer, however, did not occur even after spalling of most IMCs.
引用
收藏
页码:2428 / 2436
页数:8
相关论文
共 90 条
[1]  
Baker-Pole M.(1984)Printed circuits-origin and development, Part 2 Circuit World 10 8-undefined
[2]  
Shimade Y.(1983)Low firing temperature multiplayer glass-ceramic substrate IEEE Trans-CHMT. 6 382-undefined
[3]  
Utsumi K.(1980)Growth kinetics of intermetallic phases at the liquid Sn and solid Ni interface Scripta Met. 14 421-undefined
[4]  
Suzuki M.(1996)Interfacial reactions during soldering with lead-tin eutectic and lead (Pb)-free, tin-rich solders J. Electron. Mater. 25 1113-undefined
[5]  
Takamizowa H.(2002)Interfacial microstructure evolution between eutectic SnAgCu solder and Al/Ni(V)/Cu thin films J. Mater. Res. 17 1612-undefined
[6]  
Nitta M.(2002)Influence of substrate metallization on diffusion and reaction at the under-bump metallization/solder interface in flip-chip packages J. Mater. Res. 17 2757-undefined
[7]  
Watari T.(2000)Morphology of interfacial reaction between lead-free solders and electroless Ni-P under bump metallization J. Appl. Phys. 88 6359-undefined
[8]  
Kang S.K.(2001)Dissolution and interfacial reactions of thin-film Ti/Ni/Ag metallizations in solder joints Acta Mater 49 2609-undefined
[9]  
Ramachandran V.(2003)Effect of reaction time and P content on mechanical strength of the interface formed between eutectic Sn-Ag solder and Au/electroless Ni(P)/Cu bond pad J. Appl. Phys. 94 4108-undefined
[10]  
Kang S.K.(1999)Direct correlation between mechanical failiure and metallurgical reaction in flip chip solder joints J. Appl. Phys. 85 3882-undefined