Cathodic-Polarization Effects on the Long/Short Corrosion-Fatigue Crack Growth Rate of an Offshore Steel

被引：0
|
作者：
H. Hu
R. Akid
机构：
来源：
Materials Science | 2001年 / 37卷
关键词：
Hydrogen; Growth Rate; Aqueous Solution; Surface Crack; Crack Growth Rate;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We study the cyclic crack growth rate of an offshore steel. Compact specimens with long cracks and cylindrical specimens with short surface cracks were tested in air (at frequencies of 5–10 Hz) and in a 3.5% aqueous solution of NaCl (0.2 Hz). In the presence of cathodic polarization (−950 mV/SCE), the growth rate of long cracks is higher than under the conditions of free corrosion. The plateau appearing in this case in the da/dN–ΔK diagrams indicates the presence of hydrogen embrittlement. For ΔK > 10 MPa, the growth rates of short and long cracks coincide.
引用
收藏
页码：902 / 909
页数：7
相关论文
共 50 条
  • [1] Cathodic-polarization effects on the long/short corrosion-fatigue crack growth rate of an offshore steel
    Hu, H
    Akid, R
    MATERIALS SCIENCE, 2001, 37 (06) : 902 - 909
  • [2] The effect of cathodic protection potential on corrosion fatigue crack growth rate of an offshore structural steel
    Yu, J
    Brook, R
    Cole, I
    Morabito, D
    Demofonti, G
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1996, 19 (08) : 1019 - 1029
  • [3] Crack growth direction effects on corrosion-fatigue behaviour of offshore wind turbine steel weldments
    Jacob, Anais
    Mehmanparast, Ali
    MARINE STRUCTURES, 2021, 75
  • [4] EFFECT OF CATHODIC POTENTIAL ON CORROSION-FATIGUE CRACK GROWTH IN A516-60 STEEL
    SULLIVAN, AM
    CROOKER, TW
    REPORT OF NRL PROGRESS, 1976, (OCT): : 5 - 6
  • [5] Evaluation of Frequency Effects on Corrosion-Fatigue Behaviour of Offshore Steel Pipelines
    Mehmanparast, Ali
    PROCEEDINGS OF ASME 2024 43RD INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, OMAE2024, VOL 3, 2024,
  • [6] Corrosion-fatigue crack growth in titanium alloys
    Gregory, JK
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1999, 50 (01): : 7 - 11
  • [7] CORROSION-FATIGUE OF STIFFENED OFFSHORE STEEL TUBULAR JOINTS
    MURTHY, DSR
    RAO, AGM
    SANTHAKUMAR, AR
    JOURNAL OF STRUCTURAL ENGINEERING-ASCE, 1994, 120 (07): : 1991 - 2010
  • [8] EFFECT OF SPECIMEN THICKNESS ON CORROSION-FATIGUE CRACK GROWTH-RATE IN A516-60 STEEL
    SULLIVAN, AM
    CROOKER, TW
    REPORT OF NRL PROGRESS, 1976, (JUL): : 18 - 20
  • [9] EFFECTS OF CATHODIC POTENTIAL AND CALCAREOUS DEPOSITS ON CORROSION FATIGUE CRACK GROWTH RATE IN SEAWATER FOR TWO OFFSHORE STRUCTURAL STEELS.
    Murakami, R.
    Ferguson, W.G.
    Fatigue and Fracture of Engineering Materials and Structures, 1987, 9 (06): : 477 - 488
  • [10] THE EFFECT OF CATHODIC POLARIZATION ON CORROSION-FATIGUE OF A HIGH-STRENGTH STEEL IN SALT-WATER
    WANG, YZ
    AKID, R
    MILLER, KJ
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1995, 18 (03) : 293 - 303
12345