Dissolution behavior of zirconia-refractories during continuous casting of steel

被引：0
作者：
Anh -Hoa Bui
Sang -Chae Park
In -Sang Chung
Hae -Geon Lee
机构：
[1] Hanoi University of Technology,Department of Iron and Steelmaking Technology
[2] Pohang University of Science and Technology,Department of Materials Science and Engineering
[3] Kyungpook National University,Department of Materials Science and Metallurgy
[4] Pohang University of Science and Technology,Graduate Institute of Ferrous Technology (GIFT)
来源：
Metals and Materials International | 2006年 / 12卷
关键词：
ZrO; -graphite refractories; submerged entry nozzle (SEN); rotating cylinder method; dissolution rate; mold flux;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Dissolution behavior of ZrO2-graphite refractories used in a submerged entry nozzle (SEN) during continuous casting of steel was investigated using the rotating cylinder method. In the present work, the dissolution rate of the zirconia-graphite rod was determined by measuring the corrosion depth of the rod after a given immersion time. It was found that the dissolution rate was slow at the surface where molten flux alone is contacted, but much higher at the region that contacts the interface of the molten flux and liquid metal. The dissolution rate was influenced by the rotation speed of the rod, ZrO2 content in the refractories, and the presence of Na2O and fluoride (F−) in the mold flux. It is speculated that a cyclic process wherein zirconia dissolves into the molten flux and graphite dissolves into the liquid metal accelerates the dissolution at the flux-metal interface.
引用
收藏
页码：435 / 440
页数：5
相关论文
共 44 条
  • [1] Mukai K.(1989)undefined ISIJ Int. 29 469-469
  • [2] Toguri J. M.(1997)undefined ISIJ Int. 37 102-102
  • [3] Stubina N. M.(2000)undefined J. Euro. Ceram. Soc. 20 159-159
  • [4] Yoshitomi J.(1998)undefined Phil. Trans. R. Soc. Lond. A 356 1015-1015
  • [5] Dick A. F.(1986)undefined Trans. ISIJ 26 1052-1052
  • [6] Yu X.(1994)undefined ISIJ Int. 34 853-853
  • [7] Pomfret R. J.(1996)undefined ISIJ Int. 36 S109-836
  • [8] Coley K. S.(2004)undefined ISIJ Int. 44 836-262
  • [9] Aneziris C. G.(1999)undefined Ironmak Steelmak. 26 262-41
  • [10] Pfaff E. M.(2002)undefined JOM 54 41-183
12345