Simple preparation of highly efficient MAxFA1−xPbI3 perovskite films from an aqueous halide-free lead precursor by all dip-coating approach and application in high-performance perovskite solar cells

被引:0
作者
Zobia Irshad
Muhammad Adnan
Jae Kwan Lee
机构
[1] Chosun University,Department of Chemistry, Graduate School
[2] Chosun University,Department of Chemistry Education
来源
Journal of Materials Science | 2022年 / 57卷
关键词
D O I
暂无
中图分类号
学科分类号
摘要
All sequential-dip-coating deposition of mixed organic cationic MAxFA1−xPbI3 perovskite films from an aqueous non-halide lead precursor solution was effectively developed. Efficient crystal phase and surface morphologies of MAxFA1−xPbI3 perovskite films were successfully realized by varying MAI/FAI molar ratios in precursor solution over as-prepared Pb(NO3)2 layer. The various grain sizes and boundaries as well as cubical lumps of MAxFA1−xPbI3 perovskite crystal were also modulated after annealing at 120 °C of produced MAxFA1−xPbI3 perovskite films formed with suitable concentrations of MAI and FAI solution. Interestingly, all-dip-coating-treated MAxFA1−xPbI3 perovskite layers have no presence of δ-FAPbI3 perovskites, even at low MAI insertion into the FAI solution. Efficient device performances and improved stability with a power conversion efficiency of ~ 14.1% in perovskite solar cell devices with the all-dip-coating processed MA0.5FA0.5PbI3 perovskite layers realized by incorporating Pb(NO3)2 layers into MAI/FAI (1/1 molar ratio) solution.
引用
收藏
页码:1936 / 1946
页数:10
相关论文
共 139 条
[1]  
Okamoto Y(2018)Perovskite solar cells prepared by advanced three-step method using additional HC (NH2) 2I spin-coating: efficiency improvement with multiple bandgap structure ACS Appl Energy Mater 3 1389-1394
[2]  
Yasuda T(2016)Effects of formamidinium and bromide ion substitution in methylammonium lead triiodide toward high-performance perovskite solar cells Nano Energy 22 328-337
[3]  
Sumiya M(2017)Mixed-organic-cation (FA) ACS Appl Mater Interfaces 3 2449-2458
[4]  
Suzuki Y(2018)(MA) Chin Phys B 27 024208-9178
[5]  
Yang Z(2015)PbI3 planar perovskite solar cells with 16.48% efficiency via a low-pressure vapor-assisted solution process J Mater Chem A 17 9171-126
[6]  
Chueh C(2018)Fabrication of mixed perovskite organic cation thin films via controllable cation exchange J Colloid Interface Sci 510 118-27157
[7]  
Liang PW(2016)Temperature dependence of hole conductor free formamidinium lead iodide perovskite based solar cells Phys Chem Chem Phys 39 27148-210
[8]  
Crump M(2016)Application of mixed-organic-cation for high performance hole-conductor-free perovskite solar cells J Phys Chem Lett 7 204-2258
[9]  
Lin F(2016)Influence of the mixed organic cation ratio in lead iodide based perovskite on the performance of solar cells Adv Mater 28 2253-806
[10]  
Zhu Z(2017)Unraveling charge carriers generation, diffusion, and recombination in formamidinium lead triiodide perovskite polycrystalline thin film ACS Energy Lett 2 802-1057