Use of heat-resistant chromium-aluminum steel for tube spacers in superheaters of boiler units

被引：0
|
作者：
Kuznetsov E.V. [1 ]
Orlov A.S. [1 ]
Zagretdinov I.Sh. [2 ]
机构：
[1] JSC NPO TsNIITMASh, Moscow
[2] JSC RAO EÉS Rossii, Moscow
来源：
Power Technology and Engineering | 2007年 / 41卷 / 6期
关键词：
Bending; Boiler units; Chromium-aluminum steel; Heat resistance; Sheets; Spacers; Welding;
D O I：
10.1007/s10749-007-0066-4
中图分类号：
学科分类号：
摘要：
Results of investigations and industrial testing of heat-resistant chromium-aluminum steel 03Kh18Yu3BT are presented; from these results, this steel can be recommended for the fabrication of spacers, mounting hardware for the heating surfaces of the superheaters of boiler units, and other lightly loaded articles operating at high temperatures during the burning of all types of fuels used in the firing of thermoelectric power plants. © Springer Science+Business Media, Inc. 2007.
引用
收藏
页码：367 / 370
页数：3
相关论文
共 50 条
  • [41] SUITABILITY OF HEAT-RESISTANT TEMPERED STEEL WITH 9-12-PERCENT CHROMIUM FOR COMPONENTS IN THE CORE OF FAST BREEDER-REACTORS - REVIEW
    ANDERKO, K
    JOURNAL OF NUCLEAR MATERIALS, 1980, 95 (1-2) : 31 - 43
  • [42] Influence of holding time of annealing treatment on microstructure and properties of TIG welded joint for P91 heat-resistant steel tube
    Liu, Peng
    Sun, Siyu
    Xu, Shubo
    Cao, Meiqing
    Feng, Keyun
    KOVOVE MATERIALY-METALLIC MATERIALS, 2018, 56 (04): : 245 - 252
  • [43] Failure Analysis of TP347H Austenitic Heat-Resistant Steel Tube in a 600 MW Subcritical Thermal Power Unit
    Jun Zhang
    Jingming Yan
    Jianwei Zhang
    Zhunbei Zheng
    Zhanjun Yang
    Ning Zhou
    Journal of Failure Analysis and Prevention, 2024, 24 : 650 - 658
  • [44] Failure Analysis of TP347H Austenitic Heat-Resistant Steel Tube in a 600 MW Subcritical Thermal Power Unit
    Zhang, Jun
    Yan, Jingming
    Zhang, Jianwei
    Zheng, Zhunbei
    Yang, Zhanjun
    Zhou, Ning
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2024, 24 (02) : 650 - 658
  • [45] Use of Electrolytic Hydrogenation to Visualize the Damage of Long-Term Operated Heat-Resistant Steel of TPP Steam Pipelines
    I. O. Tsybailo
    L. M. Svirska
    P. R. Solovei
    S. R. Krechkovska
    B. M. Datsko
    O. Z. Student
    Materials Science, 2023, 58 : 602 - 608
  • [46] Use of Electrolytic Hydrogenation to Visualize the Damage of Long-Term Operated Heat-Resistant Steel of TPP Steam Pipelines
    Tsybailo, I. O.
    Svirska, L. M.
    Solovei, P. R.
    Krechkovska, S. R.
    Datsko, B. M.
    Student, O. Z.
    MATERIALS SCIENCE, 2023, 58 (05) : 602 - 608
  • [47] Improvement of the Service Properties of the Weld Joint Metal for Transport Nuclear Power Units Manufactured of Heat-Resistant Steel Grades: Part I. Technology of Welding Heat-Resistant Steel Grades Using Low-Carbon Welding Materials without Heat Treatment and Experience of Applying Welding Materials
    Timofeev M.N.
    Karzov G.P.
    Galiatkin S.N.
    Mikhaleva E.I.
    Litvinov S.G.
    Aleksandrin A.G.
    Bashulin D.L.
    Shubin O.V.
    Inorganic Materials: Applied Research, 2018, 9 (6) : 1142 - 1147
  • [48] Creep deformation and rupture behavior of 10Cr-3Co-2W heat-resistant steel weldments in ultra supercritical power units
    Huang, Yanyan
    Zhan, Yucun
    Luo, Xiaowu
    Xiong, Jiankun
    Yang, Jianping
    Mao, Guijun
    Yang, Lin
    Nie, Fuheng
    ENGINEERING FAILURE ANALYSIS, 2022, 133
  • [49] Performance on new heat-resistant steel HR3C in the ultra-supercritical units after service at high temperature for 25000 hours
    Yin, Zun
    Cai, Hui
    Liu, Hongguo
    Zhongguo Dianji Gongcheng Xuebao/Proceedings of the Chinese Society of Electrical Engineering, 2011, 31 (29): : 103 - 109
  • [50] DEVELOPMENT OF HIGH-STRENGTH 12CR-1MO-1W-V-NB STEEL TUBE FOR BOILER .2. MECHANICAL-PROPERTIES AND HOT CORROSION BEHAVIOR OF 12-PERCENT CR HEAT-RESISTANT STEELS FOR BOILER AFTER SERVICE EXPOSURE
    MASUYAMA, F
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (05): : S665 - S665
12345