Constructing atomically dispersed active sites with densely exposed and dispersed double metal-Sx catalytic sites for favorable OER catalytic activity remains rare and challenging. Herein, we design and construct a Fe1Sx@Co3S4 electrocatalyst with Fe single atoms epitaxially confined in Co3S4 nanosheets for catalyzing the sluggish alkaline oxygen evolution reaction(OER). Consequently, in ultralow concentration alkaline solutions(0.1 mol/L KOH), such a catalyst is highly active and robust for OER with low overpotentials of 300 and 333 mV at current densities of 10 and 30 mA/cm2, respectively, accompanying long-term stability without significant degradation even for 350 h. In addition, Fe1Sx@Co3S4 shows a turnover frequency(TOF) value of 0.18 s−1, nearly three times that of Co3S4(0.07 s−1), suggesting the higher atomic utilization of Fe single atoms. Mössbauer and in-situ Raman spectra confirm that the OER activity of Fe1Sx@Co3S4 origins from a thin catalytic layer of Co(Fe)OOH that interacts with trace-level Fe species in the electrolyte, creating dynamically stable active sites. Combined with experimental characterizations, it suggests that the most active S-coordinated dual-metal site configurations are 2S-bridged (Fe-Co)S4, in which Co-S and Fe-S moieties are shared with two S atoms, which can strongly regulate the adsorption energy of reaction intermediates, accelerating the OER reaction kinetics.