Fracture properties of graphite materials and analysis of crack growth under bending conditions

被引：0
作者：
E. V. Lomakin
M. P. Tretyakov
机构：
[1] Lomonosov Moscow State University,Department of Mechanics and Mathematics
[2] Perm National Research Polytechnic University,Center of Experimental Mechanics
来源：
Meccanica | 2016年 / 51卷
关键词：
Structural graphite materials; Elastic properties; Strength; Fracture toughness; Stable crack growth; Unstable crack growth;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The elastic and strength properties of different grades of graphite materials as well as their fracture toughness properties are studied. The method for the determination of crack length and the values of fracture toughness characteristics of materials during stable equilibrium crack growth under bending conditions is considered. The unstable or non-equilibrium crack growth from short initial crack is observed in experiments, and corresponding theoretical explanation is given. The process of unstable crack growth is analyzed for different loading conditions. It has been shown that in the cases of short cracks, some part of stored energy transforms into kinetic energy, which can be described by the equation of energy balance during unstable crack growth.
引用
收藏
页码：2353 / 2364
页数：11
相关论文
共 70 条
[11]  
Alexandrov S(2012)Fracture behavior of radiolytically oxidized reactor core graphites: a view Energy Mater Mater Sci Eng Energy Syst 5 899-907
[12]  
Jeng Y(2012)Fracture toughness of nuclear graphite NBG-18 Proc Int Conf Nucl Eng 1 393-397
[13]  
Lomakin E(2012)An experimental study on fracture toughness of a fine-grained isotropic graphite Proc Int Conf Nucl Eng 2 175-179
[14]  
Lomakin E(2008)Observation of microstructure deformation and damage in nuclear graphite Eng Frac Mech 75 3633-3645
[15]  
Beliakova T(2011)Damage, crack growth and fracture characteristics of nuclear grade graphite using the Double Torsion technique J Nucl Mater 414 32-43
[16]  
Belyakova TA(1983)Experimental determination of the fracture process zone in concrete Cem Concr Res 13 557-567
[17]  
Lomakin EV(1999)Nondestructive techniques for studying fracture processes in concrete Int J Fract 98 351-359
[18]  
Freiman SW(1995)Evaluation of damage in Brazilian test using holographic interferometry ACI Mater 12 268-275
[19]  
Mecholsky JJ(2014)Characterization of R-curve behavior of translaminar crack growth in cross-ply composite laminates using digital image correlation Eng Frac Mech 117 51-70
[20]  
Hodkinson PH(2011)Combined model for hardening, softening and damage processes in advanced heat resistant steel at elevated temperature Int J Damage Mech 20 578-597
1234567