Ti6Al4V Coating on 316L Substrate by Laser-based Fusion Process

被引：0
作者：
Riddhi Shukla
Konda Gokuldoss Prashanth
机构：
[1] Tallinn University of Technology,Department of Mechanical and Industrial Engineering
[2] Erich Schmid Institute of Materials Science,CBCMT, School of Mechanical Engineering
[3] Austrian Academy of Sciences,undefined
[4] Vellore Institute of Technology,undefined
来源：
Transactions of the Indian Institute of Metals | 2023年 / 76卷
关键词：
Additive manufacturing; Laser powder bed fusion; Coating; AISI 316L; Ti6Al4V;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The laser powder-bed fusion (LPBF) process is one of the additive manufacturing processes used to produce intricate geometry without limits. LPBF processes materials layer-by-layer and can fabricate a wide spectrum of materials. However, its applicability as a coating method is rarely considered. The present study aims to fabricate Ti6Al4V coating on a 316L substrate. 316L plates were fabricated using the spark plasma sintering (SPS) process and are used as the substrate for the Ti6Al4V coating. The Ti6Al4V coating was performed on the substrate with/without laser pre-scanning using laser powder-bed fusion. Cracks were observed if the coating was performed without pre-scanning of the substrate and with pre-scanning the cracks disappear. A strong interfacing bonding was observed with the formation of FeTi and Fe2Ti intermetallic phases, which enhances the hardness of the coating. The compressive results show that both SPS 316L and Ti6Al4V coating on 316L show similar curves except that the sample with coating exhibits higher deformability. The present results portray the effectiveness of the LBPF process for coating purposes.
引用
收藏
页码：435 / 445
页数：10
相关论文
共 357 条
[1]  
Gokuldoss PK(2017)Selective laser melting of high-performance pure tungsten: parameter design, densification behavior and mechanical properties Materials 10 672-224
[2]  
Kolla S(2017)undefined Technol (Basel) 5 8-35
[3]  
Eckert J(2018)undefined Prog Mater Sci 92 112-160
[4]  
Prashanth K(2016)undefined Technol (Basel) 4 34-67
[5]  
Scudino S(2017)undefined Acta Mater 126 25-2034
[6]  
Chatterjee R(2022)undefined Addit Manuf 58 103013-164
[7]  
Salman OO(2022)undefined Ceram Int 590 153-204
[8]  
Eckert J(2014)undefined Mater Sci Eng A 13 1-41
[9]  
DebRoy T(2020)undefined Materials 30 2001-380
[10]  
Wei HL(2020)undefined Trans Nonferrous Metals Soc China 37 101725-undefined
12345678910