Electrochemical investigation of the epoxy nanocomposites containing MnAl2O4 and CoAl2O4 nanopigments applied on the aluminum alloy 1050

被引：0

作者：

E. Ghasemi

B. Ramezanzadeh

S. Saket

S. Ashhari

机构：

[1] Institute for Colour Science and Technology,Inorganic Pigment and Glazes Department

[2] Institute for Colour Science and Technology,Department of Surface Coatings and Corrosion

来源：

Journal of Coatings Technology and Research | 2016年 / 13卷

关键词：

Aluminum alloy; Nanostructured pigment; Epoxy nanocomposite; Corrosion resistance; EIS;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The MnAl2O4 and CoAl2O4 nanopigments were synthesized through solution combustion method. The nanopigments extracts in the 3.5 wt% NaCl solution were prepared. Electrochemical impedance spectroscopy (EIS) and linear polarization (LP) techniques were utilized to investigate the corrosion inhibition properties of the pigments in the solutions containing pigments extracts. The epoxy nanocomposites were prepared and applied on the aluminum specimens. EIS and pull-off measurements were performed to characterize the corrosion protection properties of the epoxy nanocomposites. It was revealed that the MnAl2O4 pigment showed higher corrosion inhibition properties than CoAl2O4 in the solution phase. In addition, MnAl2O4 enhanced the corrosion resistance and decreased the adhesion loss of the epoxy coating on the aluminum substrate significantly. The MnAl2O4 nanopigment improved the corrosion resistance of the epoxy coating through increasing the barrier performance and releasing inhibitive species.

引用

页码：97 / 114

页数：17

共 50 条

[1] Electrochemical investigation of the epoxy nanocomposites containing MnAl2O4 and CoAl2O4 nanopigments applied on the aluminum alloy 1050
Ghasemi, E.
Ramezanzadeh, B.
Saket, S.
Ashhari, S.
JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, 2016, 13 (01) : 97 - 114
[2] Revisiting the ground state of CoAl2O4: Comparison to the conventional antiferromagnet MnAl2O4
MacDougall, G. J.
Aczel, A. A.
Su, Yixi
Schweika, W.
Faulhaber, E.
Schneidewind, A.
Christianson, A. D.
Zarestky, J. L.
Zhou, H. D.
Mandrus, D.
Nagler, S. E.
PHYSICAL REVIEW B, 2016, 94 (18)
[3] Elaboration of cobalt spinel CoAl2O4 and manganese spinel MnAl2O4 membranes for ultrafiltration.
Chemlal, S
Sghyar, M
Rafiq, M
Larbot, A
Cot, L
ANNALES DE CHIMIE-SCIENCE DES MATERIAUX, 2000, 25 (07): : 577 - 582
[4] STABILITIES OF MNAL2O4 AND MNCR2O4 AT 1250 DEGREES C AS DERIVED FROM EQUILIBRIUM MEASUREMENTS IN COAL2O4-MNAL2O4 AND COCR2O4-MNCR2O4 SOLID SOLUTIONS
BIGGERS, JV
MUAN, A
AMERICAN CERAMIC SOCIETY BULLETIN, 1966, 45 (04): : 371 - &
[5] Performance and Stability of Wet-Milled CoAl2O4, Ni/CoAl2O4, and Pt,Ni/CoAl2O4 for Soot Combustion
Alvarez-Docio, Carmen M.
Portela, Raquel
Reinosa, Julian J.
Rubio-Marcos, Fernando
Pascual, Laura
Fernandez, Jose E.
CATALYSTS, 2020, 10 (04)
[6] INVESTIGATION OF COAL2O4, CU/COAL2O4 AND CO/COAL2O4 CATALYSTS FOR THE FORMATION OF OXYGENATES FROM A CARBON MONOXIDE-CARBON DIOXIDE-HYDROGEN MIXTURE
BAKER, JE
BURCH, R
NIU, YQ
APPLIED CATALYSIS, 1991, 73 (01): : 135 - 152
[7] Highly Dispersed Re-Doped CoAl2O4 Nanopigments: Synthesis and Chromatic Properties
Tong, Yuping
Zhang, Hailong
Wang, Shun
Chen, Zheng
Bian, Baixue
JOURNAL OF NANOMATERIALS, 2016, 2016
[8] Low temperature thermal and volumetric behavior of MnAl2O4 spinel
Navarro, Rogerio C. S.
de Auillez, Roberto R.
Goes, Thiago Freire
Gomes, Angelo M. S.
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2020, 9 (03): : 4194 - 4205
[9] CoAl2O4 blue nanopigments prepared by liquid-feed flame spray pyrolysis method
Granados, Natalia Betancur
Yi, Eongyu
Laine, Richard
Baena, Oscar Jaime Restrepo
MATERIA-RIO DE JANEIRO, 2015, 20 (03): : 580 - 587
[10] Irradiation synthesis and characterization of CoAl2O4:Ce and Mn-codoped CoAl2O4:Ce phosphors
Wang, Yong
Wang, Shifa
Yu, Xianlun
Tang, Shengnan
Han, Subin
Yang, Liang
OPTIK, 2020, 210

← 1 2 3 4 5 →