On the Interplay Between Adhesion Strength and Tensile Properties of Thermal Spray Coated Laminates—Part II: Low-Velocity Thermal Spray Coatings

In this two-part study, uniaxial tensile testing was used to evaluate coating/substrate bonding and compared with traditional ASTM C633 bond pull test results for thermal spray (TS) coated steel laminates. In Part I, the rationale, methodology, and applicability of the test to high-velocity TS coatings were demonstrated. In this Part II, the method was investigated for low-velocity TS processes (air plasma spray and arc spray) on equivalent materials. Ni and Ni-5wt.%Al coatings were deposited on steel substrates with three different roughness levels and tested using both uniaxial tensile and ASTM C633 methods. The results indicate the uniaxial tensile approach provides useful information about the nature of the coating/substrate bonding and goes beyond the traditional bond pull test in providing insightful information on the load sharing processes across the interface. Additionally, this proposed methodology alleviates some of the longstanding shortcomings and potentially reduces error associated with the traditional ASTM C633 test. The mechanisms governing the load transfer between the substrate and the coating were investigated, and the influence of Al in the coating material evaluated.