Thermal stability of nanocrystalline 3R-CuCrO2

被引:0
作者
D. Ursu
M. Miclau
机构
[1] National Institute for Research and Development in Electrochemistry and Condensed Matter,
[2] Timisoara,undefined
[3] Politehnica University of Timisoara,undefined
来源
Journal of Nanoparticle Research | 2014年 / 16卷
关键词
Nanocrystallinematerials; Hydrothermal synthesis; Thermal stability; Grain growth;
D O I
暂无
中图分类号
学科分类号
摘要
The thermal stability of nanocrystalline 3R-CuCrO2 obtaining by hydrothermal method was investigated by annealing treatment, XRD, FT-IR, XPS and TG. The three temperature domains corresponding to thermal stability of 3R-CuCrO2 nanocrystals (25–400 °C), destabilization of nanocrystalline 3R-CuCrO2 phase (400–800 °C) and recrystallization of 3R-CuCrO2 in microcrystalline state over 800 °C, were determined by the specific hydrothermal synthesis conditions. This study has indicated that nanocrystals with delafossite structure synthesized by hydrothermal method exhibit nanocrystalline state up to a reasonably high temperature, about 390 °C, which could be interesting for technical applications and the classical theory of the grain growth.
引用
收藏
相关论文
共 65 条
  • [1] Allen GC(1973)X-ray photoelectron spectroscopy of chromium oxygen systems J Chem Soc Dalton Trans 16 1675-1683
  • [2] Curtis MT(2011)Silver doped lanthanum chromites by microwave combustion method Ceram Int 37 3037-3043
  • [3] Hooper AJ(2000)Formation of Cr(II) species in the H J Therm Anal Calorim 60 541-547
  • [4] Tucker PM(1997)/CrO J Am Ceram Soc 80 149-156
  • [5] Athawale AA(1998) system J Phys Chem B102 10672-10679
  • [6] Desai PA(1986)Sinter forging of nanocrystalline zirconia: I experimental J Mater Sci 21 2753-2758
  • [7] Fouad NE(2000)The nature of the chromium species formed during the thermal activation of chromium-promoted tin (IV) oxide catalysts: an EPR and XPS study Acta Mater 48 1239-1246
  • [8] Hague DC(1997)Oxygen potentials, Gibbs’ energies and phase relations in the Cu–Cr–O system Nature 389 939-942
  • [9] Mayo MJ(2012)Effect of initial grain size on sintering trajectories Mater Lett 70 40-43
  • [10] Harrison PG(2008)P-type electrical conduction in transparent thin films of CuAlO Appl Catal B 78 61-72