Effects of etidronate, NaOCl, EDTA irrigation solutions and their combinations on cyclic fatigue resistance of nickel–titanium single-file rotary and reciprocating instruments at body temperature

被引：0
作者：
Cevat Emre Erik
Taha Özyürek
机构：
[1] Süleyman Demirel University,Department of Endodontics, Faculty of Dentistry
[2] Istanbul Medeniyet University,Department of Endodontics, Faculty of Dentistry
来源：
Odontology | 2019年 / 107卷
关键词：
Cyclic fatigue resistance; Irrigating solution; Reciproc Blue; HyFlex EDM; WaveOne Gold;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The aim of the present study was to compare the effect of etidronic acid (HEBP), NaOCl, and EDTA solutions and their combinations on cyclic fatigue resistance of NiTi RPC Blue (RPC Blue), HyFlex EDM (HEDM), and WaveOne Gold (WOG) instruments having different metallurgic characteristics at the body temperature (37 °C). 100 WOG, 100 RPC Blue, and 100 HEDM NiTi files were randomly divided into 5 groups and immersed in the following solutions: group 1, distilled water; group 2, 6% NaOCl; group 3, 17% EDTA; group 4, 18% HEBP; group 5, 6% NaOCl and 18% HEBP. Then the instruments were rotated in an artificial canal until fracture occurred and the number of cycles to fracture was calculated. A univariate analysis of variance and post hoc Tukey tests were then performed for comparisons using SPSS 21.0 software with the significance level set at P < .05. In all the conditions, there was no difference between the cyclic fatigue resistance of WOG and RPC Blue files (P > .05). In the intragroup comparison, WOG, RPC Blue, and HEDM files showed significantly low cyclic fatigue resistance in group 5 compared to other groups (P < .05). Among the groups, there was no statistically significant difference in the fracture lengths (P > .05). EDTA, NaOCl and HEBP solutions did not affect the cyclic fatigue resistance of the tested files when used without combination. However, the combination of NaOCl and HEBP solutions significantly reduced the cyclic fatigue resistance of the tested files.
引用
收藏
页码：190 / 195
页数：5
相关论文
共 138 条
  • [1] Schäfer E(2006)Comparative study on the shaping ability and cleaning efficiency of rotary Mtwo instruments. Part 1. Shaping ability in simulated curved canals Int Endod J 39 196-02
  • [2] Erler M(2018)Cyclic fatigue resistances of Hyflex EDM, WaveOne gold, Reciproc Blue and 2shape NiTi rotary files in different artificial canals Odontology 43 1192-1196
  • [3] Dammaschke T(2018)Cyclic fatigue of reciproc and reciproc blue nickel–titanium reciprocating files at different environmental temperatures J Endod 49 483-493
  • [4] Özyürek T(2017)Cyclic fatigue resistance of OneShape, HyFlex EDM, WaveOne Gold, and Reciproc Blue nickel–titanium instruments J Endod 42 156-159
  • [5] Gündoğar M(2016)HyFlex EDM: superficial features, metallurgical analysis and fatigue resistance of innovative electro discharge machined NiTi rotary instruments Int Endod J 55 307-312
  • [6] Uslu G(2016)Torsional and cyclic fatigue resistance of a new nickel–titanium instrument manufactured by electrical discharge machining J Endod 32 389-398
  • [7] Yılmaz K(1983)Bacteriologic evaluation of the effect of 0.5 percent sodium hypochlorite in endodontic therapy Oral Surg Oral Med Oral Pathol Oral 34 208-211
  • [8] Staffoli S(2006)Root canal irrigants J Endod 10 121-128
  • [9] Grande NM(2008)Pitting corrosion resistance of nickel–titanium rotary instruments with different surface treatments in seventeen percent ethylenediaminetetraacetic acid and sodium chloride solutions J Endod 37 705-710
  • [10] Plotino G(1983)The chloride corrosion behaviour of four orthodontic wires J Oral Rehabil 39 693-699
12345678910