Effect of solution treatment on microstructures and mechanical properties of 2099 Al-Li alloy

被引:30
作者
Lin, Y. [1 ]
Zheng, Z. Q. [1 ]
Li, S. C. [1 ]
机构
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Hunan, Peoples R China
关键词
2099 Al-Li alloy; Solution treatment; Microstructures; Mechanical properties; PLASTIC-DEFORMATION; FRACTURE; MG; PRECIPITATION; EVOLUTION; BEHAVIOR; METAL;
D O I
10.1016/j.acme.2013.07.005
中图分类号
TU [建筑科学];
学科分类号
0813 ;
摘要
The influence of the solution treatment on microstructures and mechanical properties of 2099 Al-Li alloy was investigated by means of optical microscopy, scanning electron microscopy, transmission electron microscopy and tensile properties measurement. With increasing solution temperature, the quantity of primary particles in the alloy decreased, and the degree of recrystallization gradually increased, leading to softening of solution treated alloy. Dissolution of primary particles in the solution treatment process promoted delta' and T-1 phases to precipitate during sequent aging treatment resulting in increase of strength. The number of T-1 phases increased to peak value when the alloy was solution treated at 540 degrees C because almost no further dissolution of Cu-containing particles occurred at higher temperature. However, exorbitant solution temperature caused the drastic increase in the size and quantity of recrystallized grains that softened the alloy. Thus, mechanical properties of aged alloy were determined by two mechanisms: precipitation strengthening and solution softening. Compared with solution temperature, solution time had less effect on microstructures and mechanical properties of alloy. The suitable solution treatment for 2099 Al-Li alloy was 540 degrees C for 1 h, treated by which the yield strength of the aged alloy was 604 MPa with the elongation of 7.9%. (C) 2013 Politechnika Wroclawska. Published by Elsevier Urban & Partner Sp. z.o.o. All rights reserved.
引用
收藏
页码:61 / 71
页数:11
相关论文
共 19 条
[1]  
BOURGASSER P, 1989, MATER SCI TECH SER, V5, P1102, DOI 10.1179/026708389790341021
[2]   WORK-HARDENING OF COPPER-SILICA .2. ROLE OF PLASTIC RELAXATION [J].
BROWN, LM ;
STOBBS, WM .
PHILOSOPHICAL MAGAZINE, 1971, 23 (185) :1201-&
[3]   The improvement of constituent dissolution and mechanical properties of 7055 aluminum alloy by stepped heat treatments [J].
Chen, KH ;
Liu, HW ;
Zhang, Z ;
Li, S ;
Todd, RI .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 142 (01) :190-196
[4]   The influence of Cu/Li ratio on precipitation in Al-Cu-Li-x alloys [J].
Decreus, B. ;
Deschamps, A. ;
De Geuser, F. ;
Donnadieu, P. ;
Sigli, C. ;
Weyland, M. .
ACTA MATERIALIA, 2013, 61 (06) :2207-2218
[5]   DUCTILE FRACTURE [J].
GARRISON, WM ;
MOODY, NR .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1987, 48 (11) :1035-1074
[6]   NUCLEATION OF CAVITIES BY PLASTIC-DEFORMATION - OVERVIEW [J].
GOODS, SH ;
BROWN, LM .
ACTA METALLURGICA, 1979, 27 (01) :1-15
[7]   Independent and combined roles of trace Mg and Ag additions in properties precipitation process and precipitation kinetics of Al-Cu-Li-(Mg)-(Ag)-Zr-Ti alloys [J].
Huang, BP ;
Zheng, ZQ .
ACTA MATERIALIA, 1998, 46 (12) :4381-4393
[8]   Damage characterization and modeling of a 7075-T651 aluminum plate [J].
Jordon, J. B. ;
Horstemeyer, M. F. ;
Solanki, K. ;
Bernard, J. D. ;
Berry, J. T. ;
Williams, T. N. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 527 (1-2) :169-178
[9]   Aluminum-Copper-Lithium Alloy 2050 Developed for Medium to Thick Plate [J].
Lequeu, Ph ;
Smith, K. P. ;
Danielou, A. .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2010, 19 (06) :841-847
[10]   Effect of copper content on mechanical properties and fracture behaviors of Al-Li-Cu alloy [J].
Liu, Q ;
Chen, CZ ;
Cui, JZ .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2005, 36A (06) :1389-1394