Technological provision of contact fatigue resistance for cemented gear wheels made of heat-resistant steels

被引：0
|
作者：
N. M. Ryzhov
机构：
[1] N. É. Bauman Moscow State Technical University (MGTU),
来源：
Metal Science and Heat Treatment | 2010年 / 52卷
关键词：
contact fatigue; cemented layer parameters; technology; vacuum cementation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
On the basis of analyzing the effect structural factors on the mechanism of contact fatigue of complexly-alloyed heat-resistant steels requirements are determined for cemented layer parameters corresponding to high contact fatigue resistance. The possibility is demonstrated of implementing these requirements during cyclic vacuum cementation regimes.
引用
收藏
页码：330 / 335
页数：5
相关论文
共 50 条
  • [41] Superhydrophobic surface with lotus/petal effect and its improvement on fatigue resistance of heat-resistant steel
    Li, Guijie
    Jiang, Bo
    Liu, Huiqun
    Ning, Liang
    Yi, Danqing
    Wang, Xianming
    Liu, Zhiyuan
    PROGRESS IN ORGANIC COATINGS, 2019, 137
  • [42] EFFECT OF LTMT ON HEAT-RESISTANCE AND CONTACT FATIGUE RESISTANCE OF HIGH-ALLOY BEARING STEELS
    KONTER, LY
    ARTAMONOVA, VV
    SHEIN, AS
    METAL SCIENCE AND HEAT TREATMENT, 1976, 18 (3-4) : 255 - 257
  • [43] Microstructure and Corrosion Resistance of CrN and CrN/TiN Coated Heat-Resistant Steels in Molten Aluminum Alloy
    LinCS
    PengH
    特种铸造及有色合金, 2001, (S1) : 168 - 171
  • [44] OXIDATION AND HOT CORROSION-RESISTANCE OF SOME HEAT-RESISTANT 12CR-MO STEELS
    GROBNER, PJ
    VINEBERG, EJ
    CIM BULLETIN, 1982, 75 (842): : 125 - 126
  • [45] FATIGUE RESISTANCE OF VT9 HEAT-RESISTANT ALLOY UNDER MARINE CLIMATE CONDITIONS.
    Mazmanidi, V.T.
    Tavadze, F.N.
    Zhukov, N.D.
    Krivenko, M.P.
    Soviet materials science, 1985, 21 (03): : 255 - 257
  • [46] The influence of plasticity-induced crack closure on creep-fatigue crack growth in two heat-resistant steels
    Ramirez, J.
    Potirniche, G. P.
    Shaber, N.
    Taylor, M.
    Pugesek, H.
    Stephens, R.
    Charit, I.
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 125 : 291 - 298
  • [47] CREEP FATIGUE BEHAVIOR OF HEAT-RESISTANT STEELS UNDER SERVICE-TYPE STRAIN CYCLING AT HIGH-TEMPERATURE
    KLOOS, KH
    GRANACHER, J
    SCHOLZ, A
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 1989, 20 (04) : 118 - 125
  • [48] ESTIMATE OF RESISTANCE TO INITIAL CRACK GROWTH IN HEAT-RESISTANT STEELS UNDER ACTION OF LONG-TERM LOADS
    GLADSHTEIN, VI
    SHERBAUM, NL
    SEMENOVA, TN
    INDUSTRIAL LABORATORY, 1977, 43 (09): : 1296 - 1298
  • [49] RESISTANCE OF WELDED-JOINTS IN HEAT-RESISTANT STEELS TO CORROSION, UNDER STRESS, IN GASEOUS SULFUR-COMPOUNDS
    MIKHALIK, Y
    AUTOMATIC WELDING USSR, 1973, 26 (02): : 12 - 17
  • [50] PRESENT QUALITY LEVEL OF LARGE HEAT-RESISTANT ROTOR FORGINGS MADE OF 1-PERCENT-CRMOV STEELS .1.
    EWALD, J
    BERGER, C
    KEIENBURG, KH
    WIEMANN, W
    STEEL RESEARCH, 1986, 57 (02): : 83 - 92
12345