A combined characterization of zinc hot-dip galvanized wireswith DSC, XRD and SEM

被引：0
作者：
N. Pistofidis
G. Vourlias
E. Pavlidou
K. Chrissafis
G. Stergioudis
E. K. Polychroniadis
D. Tsipa
机构：
[1] Aristotle University of Thessaloniki,Physics Department
[2] Aristotle University of Thessaloniki,Department of Mechanical Engineering,
来源：
Journal of Thermal Analysis and Calorimetry | 2006年 / 86卷
关键词：
corrosion protection ; DSC characterization; hot-dip galvanizing; metallic coatings;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effect of Pb and Sn on the structure of zinc hot-dip galvanized coatings on steel wires is examined. The coating quality is often low because of the Sandelin effect. An improvement could be expected if 1.0 mass% Pb is added to the Zn bath. In this case the η phase formation is enhanced, while the coating thickness is reduced. The Sn addition at the same concentration promotes the formation of the η phase but it does not affect the thickness.
引用
收藏
页码：417 / 422
页数：5
相关论文
共 50 条
  • [1] A combined characterization of zinc hot-dip galvanized wires with DSC, XRD and SEM
    Pistofidis, N.
    Vourlias, G.
    Pavlidou, E.
    Chrissafis, K.
    Stergioudis, G.
    Polychroniadis, E. K.
    Tsipas, D.
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2006, 86 (02) : 417 - 422
  • [2] Verification of the Properties of Zinc Hot-Dip Galvanized Steel Samples
    Cerny, Daniel
    Kuchar, Jiri
    Kania, Henryk
    Saternus, Mariola
    ADVANCES IN MANUFACTURING IV, VOL 1, MANUFACTURING 2024, 2024, : 195 - 205
  • [3] On the effect of zinc melt composition on the structure of hot-dip galvanized coatings
    Konidaris, S.
    Pistofidis, N.
    Vourlias, G.
    Pavlidou, E.
    Stergiou, A.
    Stergioudis, G.
    Polychroniadis, E. K.
    SIX INTERNATIONAL CONFERENCE OF THE BALKAN PHYSICAL UNION, 2007, 899 : 796 - 796
  • [4] On texture, corrosion resistance and morphology of hot-dip galvanized zinc coatings
    Asgari, H.
    Toroghinejad, M. R.
    Golozar, M. A.
    APPLIED SURFACE SCIENCE, 2007, 253 (16) : 6769 - 6777
  • [5] Characterization of hot-dip galvanized coating on dual phase steels
    Liu, Huachu
    Li, Fang
    Shi, Wen
    Liu, Rendong
    Li, Lin
    SURFACE & COATINGS TECHNOLOGY, 2011, 205 (11) : 3535 - 3539
  • [6] Embrittlement of Hot-Dip Galvanized Steel: A Review
    Shreyas, P.
    Panda, Bijayani
    Vishwanatha, A. D.
    3RD INTERNATIONAL CONFERENCE ON ADVANCEMENTS IN AEROMECHANICAL MATERIALS FOR MANUFACTURING: ICAAMM-2020, 2021, 2317
  • [7] Fire resistance of hot-dip galvanized steel structures
    Mensinger, Martin
    Gaigl, Christian
    STAHLBAU, 2019, 88 (01) : 3 - 10
  • [8] Effects of Structures of Zinc/Substrate Interface on Coating Adhesion of Hot-dip Galvanized DP Steels
    Jiang, Sheming
    Li, Yuanpeng
    Zhang, Qi-Fu
    ADVANCES IN MATERIALS AND MATERIALS PROCESSING IV, PTS 1 AND 2, 2014, 887-888 : 338 - 344
  • [9] Characterization of the Fe-Al interfacial layer in a commercial hot-dip galvanized coating
    McDevitt, E
    Morimoto, Y
    Meshii, M
    ISIJ INTERNATIONAL, 1997, 37 (08) : 776 - 782
  • [10] Cracking mechanisms in high temperature hot-dip galvanized coatings
    Tzimas, E
    Papadimitriou, G
    SURFACE & COATINGS TECHNOLOGY, 2001, 145 (1-3) : 176 - 185
12345