Fabrication of copper-coated glass fabric composites through electroless plating process

被引:0
作者
Huiyu Chen
Yu Tai
Chunju Xu
机构
[1] North University of China,School of Materials Science and Engineering
来源
Journal of Materials Science: Materials in Electronics | 2017年 / 28卷
关键词
Sodium Hydroxide; HCHO; Glass Fabric; Electroless Plating; Copper Layer;
D O I
暂无
中图分类号
学科分类号
摘要
Copper-coated glass fabric was successfully fabricated via electroless plating method, and the copper layer on the surface of glass fabric was continuous and compact. The chemical composition of the copper coatings was investigated by X-ray diffraction, and the microstructures were invested by scanning electron microscopy. It was found that the quality of the copper layer was closely related to the dosage of NaOH and reducing reagent, respectively. These composites possessed excellent conductivity with the volume resistivity up to 2.57 × 10−3 Ω cm, and can be used as shielding materials.
引用
收藏
页码:798 / 802
页数:4
相关论文
共 43 条
[1]  
Rahaman A(2011)undefined Fuller. Nanotub. Carbon Nanostruct. 19 373-397
[2]  
Kar KK(2014)undefined J. Mater. Sci.: Mater. Electron. 25 4638-4642
[3]  
Xu CJ(2015)undefined Micro. Nano Lett. 10 315-317
[4]  
Zhou RH(2014)undefined J. Mater. Sci.: Mater. Electron. 25 2611-2617
[5]  
Chen HY(2016)undefined Mater. Lett. 173 211-213
[6]  
Liu GL(2016)undefined Mater. Lett. 171 158-161
[7]  
Xu CJ(2016)undefined Mater. Lett. 180 144-147
[8]  
Chen HY(2016)undefined Carbohydr. Polym. 149 51-59
[9]  
Xu CJ(2016)undefined Sens. Actuators B Chem. 225 377-383
[10]  
Liu GL(2016)undefined Appl. Surf. Sci. 362 154-162