Microstructure Evolution and Abrasive Wear Behavior of Ti-6Al-4V Alloy

This paper investigates the effect of quenching and aging treatment on microstructure and abrasive wear of Ti-6Al-4V alloy. The as-received alloy was solution treated at 1339 K, then oil quenched, followed by aging at 823 K for 4 h (14,400 s). The microstructures of as-received and quench-aged specimens were characterized by using optical microscopy, scanning electron microscopy, energy dispersive spectroscopy, and electron backscattered diffraction techniques. The as-received specimen consisted of very fine α grains (average grain size 2 μm) with β phase uniformly dispersed throughout. The microstructure of the quench-aged specimen showed α plates (formed by the decomposition of α′ during aging). The β phase precipitated out of α′ martensite during aging and hence was dispersed uniformly in the α matrix. Ti-6Al-4V alloy was quench-aged to achieve maximum hardness with a view that the increased hardness would lead to an improvement in abrasive wear behavior. Two-body abrasive wear tests were carried out on the as-received and quench-aged specimens using pin-on-disk apparatus with SiC as abrasive media (150-grit size). The effect of sliding distance and normal load on the abrasive wear behavior was studied. The wear resistance of the as-received specimen was greater than that of quench-aged specimen, while hardness of the as-received specimen was lower than that of quench-aged specimen. The abrasive wear behavior of Ti-6Al-4V alloy has been explained based on morphology/microstructure of the alloy and the associated wear mechanism(s).