Bump formation on a glass surface with a transparent coating using femtosecond laser processing

被引：0
作者：
D. Kawamura
A. Takita
Y. Hayasaki
N. Nishida
机构：
[1] The University of Tokushima,Department of Optical Science and Technology, Faculty of Engineering
来源：
Applied Physics A | 2006年 / 85卷
关键词：
PMMA; Femtosecond Laser; Glass Surface; Femtosecond Laser Pulse; Rear Surface;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The morphology of a glass surface having a transparent coating processed with focused femtosecond laser pulses is investigated. The transparent coating is formed of poly-methyl methacrylate (PMMA). When the glass was coated with a PMMA film with a thickness of 2.8 μm, bumps were formed over a wide range of axial focus positions. The same laser pulse energy produced cavities when processing bare glass with no coating. The bumps were formed as a result of suppressing material emission from the glass surface by a shielding effect of plasma generated by ablation of the PMMA film and by physical blocking of the PMMA film. A thinner film with a thickness of 0.7 μm produced a reduced shielding effect, forming an exploded bump with a small pit at its center and debris around the periphery.
引用
收藏
相关论文
共 135 条
  • [11] Obara M.(2003)undefined Appl. Phys. Lett. 82 2901-undefined
  • [12] Stuart B.C.(2003)undefined Jpn. J. Appl. Phys. 42 L1452-undefined
  • [13] Feit M.D.(2003)undefined Appl. Phys. A 77 229-undefined
  • [14] Rubenchik A.M.(2005)undefined Appl. Phys. Lett. 86 044102-1-undefined
  • [15] Shore B.W.(2005)undefined Opt. Lett. 30 1773-undefined
  • [16] Perry M.D.(2000)undefined Opt. Express 7 41-undefined
  • [17] Chichkov B.N.(2002)undefined Opt. Express 10 1244-undefined
  • [18] Momma C.(2004)undefined Jpn. J. Appl. Phys. 43 8089-undefined
  • [19] Notle S.(2006)undefined Appl. Phys. A 82 523-undefined
  • [20] von Alvensleben F.(2003)undefined Appl. Phys. A 77 223-undefined
12345678910