Preparation of lithium ion conductive Li6PS5Cl solid electrolyte from solution for the fabrication of composite cathode of all-solid-state lithium battery

被引：0
作者：
Nataly Carolina Rosero-Navarro
Akira Miura
Kiyoharu Tadanaga
机构：
[1] Hokkaido University,Division of Applied Chemistry, Faculty of Engineering
来源：
Journal of Sol-Gel Science and Technology | 2019年 / 89卷
关键词：
All solid state lithium battery; Solid electrolyte; Composite electrode; Argyrodite type;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
An argyrodite type Li6PS5Cl was prepared by solution process using a mixture solvents with a fast evaporation rate.Composite cathode for all solid state battery was directly prepared by dispersing a cathode material in the precursor solution.The cell worked as a rechargeable battery with good cycle performance.
引用
收藏
页码：303 / 309
页数：6
相关论文
共 90 条
  • [1] Sakuda A(2008)Improvement of high-rate performance of all-solid-state lithium secondary batteries using LiCoO Electrochem Solid State Lett 11 A1-A3
  • [2] Kitaura H(2017) coated with Li Chem Mater 29 3883-3890
  • [3] Hayashi A(2016)O-SiO Chem Mater 28 2634-2640
  • [4] Tadanaga K(2017) glasses J Mater Chem A 5 23919-23925
  • [5] Tatsumisago M(2014)Interface stability of argyrodite Li J Mater Chem A 2 5095-5099
  • [6] Auvergniot J(2016)PS Adv Mater 28 1874-1883
  • [7] Cassel A(2017)Cl toward LiCoO Chemsuschem 10 2605-2611
  • [8] Ledeuil JB(2017), LiNi Ceram Int 44 742-945
  • [9] Viallet V(2015)Co J Power Sources 293 941-1624
  • [10] Seznec V(2017)Mn Ionics 23 1619-4
123456789